During this process, each time the wire is pulled over, the surface hardens due to the high friction temperature. So basically every time you pull it you have to annealing it in the furnace. On the one hand, it is to reduce the surface hardness. On the other hand, during the process of wire pulling, only the surface is deformed, and the center is unchanged. So there’s a lot of stress inside. Therefore, it is necessary to rely on annealing to eliminate the internal stress, so that the wire becomes soft again to eliminate the stress before being drawn again.
Hot dip galvanizing, also known as hot dip zinc, is the method of forming a layer of zinc coating on the surface of the workpiece after oil removal and rust removal, showing a clean and infiltrating surface, immediately immersed in the plating tank of zinc melting in advance. Cold galvanizing is the same after the removal of oil, in addition to lure, showing no pollution, infiltration of the workpiece hung into a special electroplating tank on the cathode, the anode with zinc. Switch on the DC power supply, zinc ions on the anode migrate to the cathode, and discharge on the cathode, so that the workpiece is coated with a layer of zinc layer hot dip galvanizing method.
The use of bundled galvanized wire with the development of industry and agriculture also expanded accordingly. Therefore, galvanized wire products in the industry, such as chemical equipment, oil processing, Marine exploration, transport, electricity, shipbuilding, metal structure, etc.), agriculture (such as sprinkler irrigation, dim room, building (such as water and gas transport, wire casing, scaffolding, house, etc.), Bridges, shipping, etc., has been widely use in recent years. Because galvanized wire goods have beautiful surface, good corrosion resistance and other characteristics, its use scale is more and more extensive.
At present, there are two main kinds of electric galvanized wire products, hot dip galvanized wire and electric galvanized wire. The difference is that the way of galvanizing is different, and the quality of the products is different. Hot dip galvanized wire zinc layer thick, corrosion resistance is stronger, but correspondingly, the price is high. Galvanized wire zinc coating thin, corrosion resistance is poor, but the price is low.
Cold galvanizing is in the plating tank through the current unidirectional zinc gradually plated on the metal appearance, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, smooth, high aesthetics, poor corrosion resistance, generally a few months will rust. Hot dip galvanized coating is thicker, generally 30-60 microns, coating corrosion resistance is higher. Suitable for outdoor work of steel parts, such as highway fences, power towers, large size fasteners and other more “rough” workpiece long-term rust prevention.
Environmental factors should be considered when choosing the thickness of galvanized layer. Galvanized wire in galvanized, pay attention to the above problems, can be well galvanized, to ensure the quality of galvanized wire. Galvanized methods are mainly divided into two types, one is hot dip galvanizing method, the other is electric galvanizing method. This paper mainly introduces the method of galvanizing. Electrogalvanizing is an electrolyte used for galvanizing.
In the electroplating tank through the current unidirectional make zinc plating on the metal surface gradually, the production speed is slow, the coating is uniform, the thickness is thin, usually only 3-15 micron, the appearance is bright, smooth, beautiful, poor corrosion resistance, generally will rust in a few months. The production process of hot wire plating mainly includes: preparation of the original plate → pre-plating treatment → hot dip plating → post-plating treatment → finished product inspection, etc. According to custom often according to plating pretreatment method.
For the wide use of screen, the state has regulations. You also specify the diameter size, mesh size, or usage method. For plastering mesh, mesh should be less than 20 and diameter greater than 1 nm. Not only are specifications specified, but safety is preferred if wire mesh is used in exterior plastering mesh. If you fall, the consequences are unimaginable. Therefore, the application of norms should be combined with reality.
Hexagonal net structure can be used for slope support, excavation, rock face net mine support form, slope vegetation (green color), railway road isolation block, it can be made into a cage, cushion, used for rivers, flood dam and seawall erosion protection and storage reservoir, river closed cage. Driving and guiding rivers, river flood disaster is a major water and river erosion of destruction, resulting in flooding, resulting in a great deal of loss of property by the amount of soil and water dissipation. Because of this, in dealing with these problems, the application of the habitat grid structure becomes a solution plan, which has the potential to protect the bank forever.