Our country industry chooses the low carbon steel with good quality as raw material, and then produces the quality galvanized iron wire by drawing, galvanizing and other processes. Now the production technology of galvanized iron wire products can be divided into hot plating and electroplating two kinds of methods. No matter which one is chosen, it should be carried out in accordance with the corresponding operating specifications, so as to better ensure the production of good products. For key and important parts with tensile strength greater than 1034mpa before plating, the stress should be released at 200±10℃ for more than 1 hour and 140±10℃ before plating.
If it is not packaged, then a car of blade thorn rope can not be loaded with many pieces, and it is also relatively occupied and easy to lose in the transportation process. The number of the packed blade thorn rope is 50 bundles, and the volume is reduced after hydraulic compression so that it is more convenient to load and unload, and the forklift can easily load and unload. Under normal circumstances, when exporting, the blade thorn rope will be packaged and sold, so that the volume occupied in the container is relatively small, which can be easily placed and will not occupy much place.
When large rolls of galvanized wire are used to bind and reinforce the goods, corresponding binding methods should be selected according to the fastening node conditions of the strengthened goods, such as opening binding, opening binding, insertion binding and so on. The insulation layer of semi-hard and soft insulation products shall be based on the diameter of the steel pipe and the size of the equipment. Large rolls of galvanized wire or glue are tied together with a width of 60mm. The binding interval of semi-hard insulating products shall not exceed 300 mm; The larger length of felt and cushion shall not exceed 200mm, and the number of belts shall not be less than 2.
Hot dip galvanizing has been used for more than 150 years, and its principle has not changed so far. The steel structure should be fully immersed in zinc at one time to achieve uniform galvanized film structure. If it is too long or too wide to be dipped twice, the zinc layer at the joint will appear rough, too thick and so on. In addition, if the single weight of steel structure is too heavy, it will make its operation difficult if it exceeds the load of galvanizing equipment. Therefore, the communication with the hot dip galvanizing factory in advance.
Dogs of all ages seem to love to touch their noses with humans and other animals. In fact, dogs touch their noses as a way of socializing, just like humans shake hands and hug when they meet. But dogs don’t touch every human or every animal. They pick and choose who to touch. If they don’t like you or don’t know you at all, they won’t touch your nose. However, adult dogs will touch almost every puppy’s nose, and they will not only touch the puppy’s nose, but also smell it.
Galvanized iron wire is very common in practical application, some people think that galvanized iron wire will not rust, in fact, it is not. Metal corrosion is caused by the chemical or electrochemical action of the surrounding medium. According to different media, it is divided into atmospheric corrosion, soil corrosion, seawater corrosion, bacterial corrosion and so on. Atmospheric corrosion is more common, because metal products in the process of processing, transportation and storage, when in contact with the atmosphere, there are always atmospheric corrosion conditions.
Hot plating wire mixed rare earth and aluminum elements, make zinc liquid fluidity, more uniform coating, but also reduce zinc consumption. Hot-dip galvanized wire has better protective properties than cold galvanized wire, which makes it widely used in chemical experiment equipment. Hot plated wire coating is thick, so that it has good corrosion resistance, can be in the outdoor sun and rain and other harsh environment can be maintained for decades, so hot galvanized wire is widely used in construction, traffic guardrail and other outdoor facilities.
Paint on the galvanized layer, the bonding force between each other has a great relationship with the baking temperature of the paint, and alkyd paint is coated after galvanized, and the adhesion is not a problem. After galvanized to do amino paint, paint adhesion is not very good. Do two bottom two surface, adhesion is good, if the two bottom two surface changed to two bottom three surface, that is, more paint, more baked once, again test adhesion is very bad, bad enough to tear the paint from the galvanized layer.
Hexagonal guardrail network custom corrosion lost the original characteristics, in the shape, color and mechanical properties will change, resulting in equipment damage, pipeline leakage, etc., specifically, it is easy to break, lose the original protection function.
Galvanized wire A stable layer of zinc is coated on the outside of the wire, which is used to protect the wire and make the wire service life longer. When producing galvanized wire, the wire is pickled. Pickling is to use some acid mist or acid to wash off some oxides on the surface of iron, that is, rust, and some other corrosive substances, to achieve the purpose of cleaning iron, so that zinc will fall off when galvanizing.