The advantage of galvanized iron wire after annealing: after annealing increases the elongation of the iron wire. Makes the product softer and increases the range of application. After electric galvanizing hot dip galvanizing. Copper electroplating is widely used and screen production. Galvanized iron wire is a soft iron wire product processed by low carbon steel wire through cold drawing, heating, constant temperature, and even heat preservation. Generally, the quality of ordinary galvanized iron wire will be relatively soft, the softness is relatively balanced, and the color is consistent. It is mainly used in construction, mining, chemical industry and so on.
If the surface of galvanized wire hair black, galvanized layer is thin and uneven, this galvanized wire is partly because the inventory storage time is longer, it may also be because the production technical requirements of galvanized wire, do not meet the standard standards and lead to galvanized wire quality problems. According to the use of galvanized wire is different, galvanized wire has soft and hard, so the galvanized wire for binding requires the flexibility of galvanized wire is better, the flexibility of galvanized wire is good, which can facilitate the operation of workers.
Spring steel wire should have high tensile strength, elastic limit, endurance and fatigue strength, and resistance to impact and oscillation. The strength and endurance objectives, especially to prevent the occurrence of modification cracks, are the key to the consumption of spring wire. The inner quality and outer quality of the wire rod directly affect the function of the wire.
Some raw materials in the production of unstable processing, the wire itself will exist burr, surface small pits and other local defects. Galvanized steel in galvanized, generally should pay attention to the galvanized layer protection time of galvanized wire, and the thickness of galvanized layer has a great relationship. Generally speaking, when the main gas is relatively dry and used indoors, the galvanized layer thickness of galvanized wires is only 6-12μm, and under relatively harsh conditions, the galvanized layer thickness of galvanized wires needs 20μm, and can be predicted to reach 50μm.
As we all know, iron wire rust is due to contact with water and oxygen chemical reaction, therefore, how to prevent galvanized iron wire rust, first of all, in the storage of galvanized iron wire should choose ventilated dry place, avoid wet or rain leakage, in use, in addition to follow the principle of first in first out, if accidentally caused by the destruction of galvanized layer, should be coated with anti-rust paint treatment, Otherwise, it is easy to lose the protection of galvanized layer and cause galvanized iron wire rust.
In the process of composite plating, it is necessary to stir the plating solution to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. In the process of production, the acid activation solution can remove the corrosion products and oxide film on the surface of low carbon steel wire without excessive corrosion on the matrix. Galvanized wire can be used zincate galvanized or chloride galvanized and other processes, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire.
Hot wire is made of high quality low carbon steel, high carbon steel, after drawing, hot galvanized processing galvanized wire. Hot dip galvanized wire production process: wire rod – drawing – annealing – drawing – annealing – galvanized. Hot dip galvanized wire has the characteristics of thick coating, strong corrosion resistance and solid coating. And according to the special needs of users, according to the industry standard to provide various specifications of galvanized wire. Hot-dip galvanized wire is of better quality than electrodip galvanized wire. In the production process, hot dip galvanized wire has more than one annealing process, so the corrosion resistance of hot dip galvanized wire is stronger than that of electric galvanized wire.
Regular maintenance and maintenance, save a lot of time, but also save the cost of maintenance and maintenance. With good stability, good corrosion resistance, greatly prolong the service life. More kinds, can be selected according to different uses, making annealing wire device is simple, improve the utilization rate of the device.
The insulation layer of large rolls of galvanized wire and rigid thermal insulation products can be bound with double strands of galvanized iron wire, and the binding interval shall not exceed 400mm. The pipe or corresponding equipment with nominal diameter equal to or greater than 600mm shall stop reinforcement after binding, and the enclosed galvanized steel wire must be winched. The iron or wood rod should be tightened, but the tightening level should be moderate, not too tight or too loose, and not damage the wire. The consumption of wire and steel wire is generally used in drawing process and galvanized disposal.