In general, the hardness of a metal is often considered to be the resistance of the material to plastic deformation, scratches, wear, or cutting. In the debugging of zinc wire dipping distance, keep the original speed unchanged, according to the time of dipping zinc, the diameter of steel wire, and then estimate the dipping distance. By adjusting the zinc immersion distance, the zinc immersion time of steel wire of various specifications is shortened by 5s on average compared with that before debugging, so that the zinc consumption per ton of steel wire is reduced from 61kg to 59.4kg.
There is as far as possible not to show the trace of the application of wire, wire wound flower stems should be wrapped with green or brown tape, in order to cover the trace of the use of wire, in the use of wire modeling can make the drooping flower head raised, and the flower head reinforcement, for herbs and other flower material soft plants, can make the stalk straight. Wire shearing method: if you want to cut the wire, the wire should be straightened and then cut, can not bend the wire, fold and then cut, otherwise, the wire cut is not straight, will bring a small hook, affect the use.
Life said “wire”, in fact, is “low carbon steel wire”, carbon content in 0.2% below. The surface is usually coated with zinc coating because it is easy to rust. Under atmospheric conditions, the galvanized layer will not rust before most of the fall off, relatively soft. Life said “steel wire”, is the carbon content of about 0.6% of the “carbon steel wire”, or carbon content of about 0.8% of the “high carbon steel wire”, they have enough hardness and elasticity after appropriate heat treatment, high strength. The use of words such as winding ordinary spring and so on.
Generally, due to wet weather and more precipitation, oxidation and rust of binding iron wire NetEase occurs, so we should better store and use galvanized iron wire to avoid rust as far as possible. About the barbed wire, the surface of the barbed wire attached a layer of galvanized layer, the galvanized layer if too thick will not meet the SGS environmental standards. But if it is too thin, it is easy to oxidize with water molecules and rust.
The anticorrosion of these raw materials is very different, and the use of life is not the same. Niu LAN net cold galvanized, also known as electroplating, galvanized quantity is very little, rust in rain, but the price is cheap, the use of life in 5-6 years. Hot dip galvanizing (low zinc and high zinc) on the amount of zinc in 60 grams to 400 grams, the service life is about 20-60 years, corrosion resistance is general.
The best way to manage off-road safety is to carry out management and protection from the source, maximize the safety of people’s lives and property, and reduce the non-operational costs of railway enterprises, which is a key content of railway safety work in the new era. At this time, it is necessary to install protective nets on both sides of the railway, which is what we usually say, blade barbed rope protective nets, which can prevent accidents.
Cold galvanized, generally speaking, do not need heating, galvanized amount is little, this galvanized parts are easy to fall off in wet environment. Hot dip galvanizing, also known as hot dip galvanizing, is to melt the zinc ingot at high temperature, put some auxiliary materials in, and then dip the metal structural parts into the galvanized groove, so that the metal members are attached to a layer of zinc layer. The advantage of hot dip galvanized is that its anticorrosion ability is strong, the adhesion and hardness of galvanized layer is better.
On the contrary, the denser the ion deposition, the better the quality of zinc layer. Under the condition that the surface zinc layer is dense and bright, the quality of zinc layer per unit area should reach 80g/m2, and the process parameters should be optimized as follows: current density is 16-20A /dm2, mass concentration of zinc sulfate solution is 500g/L, and pH value is 2.5-3.0.
The production process of large rolls of galvanized wire is a level of drawing, through the mold into a slightly smaller diameter than the original. And so on down to the desired length. One pull is not desirable, must be numbered, from coarse to fine is dependent on metal ductility. If it changes too much it just breaks. After drawing to a certain diameter, galvanized, so that the finished product.
Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.