The external environment has great influence on the preservation of galvanized wire mesh. In the rainy season, it is necessary to pay attention to the air humidity of the workshop, warehouse and other departments. It is recommended to use a humidifier. Usually, the moisture absorption of book paper is larger than that of powder paper, and the pH value is higher. Generally speaking, in the normal environment of storage wire, storage time of two years is not corroded wire phenomenon. However, it should be noted that in the process of handling the iron wire, it should be handled gently to avoid the position of the coiling coil, which will cause the smooth pulling of the wire and affect the production.
Electrode application range is wide, can realize a variety of materials, a variety of profiles and a variety of joint forms of welding. (1) Welding between low carbon steel, low alloy steel, medium carbon steel, alloy steel and other metal materials or dissimilar metal materials can be achieved. The weld has good comprehensive mechanical properties, and the tensile strength can reach more than 400MPa. ⑵ Can realize the welding of large plate, steel frame, plate – tube, rod – rod, tube – tube and other profiles. ⑶, can realize docking, Angle, lap, T joint and other joint forms of welding. ⑷ mainly suitable for flat welding.(5) it can surfacing the parts of wear failure, so as to obtain the surface surfacing layer with melting depth, smooth surface and excellent performance. ⑹ It can be realized that no bevel 1 ~ 6mm thick metal sheet single-side welding double-side molding.
Custom is made of low carbon steel silk woven, mesh structure he has the characteristics of corrosion resistance, high strength and ductility. Steel wire diameter up to 2.0mm-4.0mm, steel wire appearance is usually selected hot dip galvanized maintenance, galvanized maintenance layer thickness can be made according to customer needs, galvanized maximum can reach 300g/㎡.
1, galvanized wire mesh molding sheet must be packed with flat hard data, to avoid eternal deformation due to poor packaging. It IS VERY IMPORTANT THAT EACH PACKAGE AND ROLL OF RAW SHEET MATERIAL BE MARKED WITH PRODUCT NAME, STANDARD, QUANTITY, TRADEMARK, batch number, MANUFACTURER, DATE of production, STACKING SYMBOL, INSPECTOR CODE AND INSPECTION CERTIFICATE.
There is no adhesion test of powder spraying or fluorocarbon spraying on packaged galvanized wire, but there are two points for reference: first, in sealed or air-free environment, non-metallic volatiles can corrode zinc coating; Second, zinc at higher than 230 degrees (c) will cause the matrix metal brittle. And powder spraying and fluorocarbon spraying are to be baked at a higher temperature and in a sealed environment, causing rapid corrosion of zinc, resulting in loose corrosion film resulting in coating adhesion decline, and even lead to (matrix) steel wire brittle situation may exist.
The difference is that hot dip galvanizing is dipped in zinc solution melted by heating, which has fast production speed and thick but uneven coating. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Cold galvanized is in the plating tank through the current unidirectional zinc gradually plated on the metal surface, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust.
The use of spring in a specific environment, there will be some special requirements for steel wire, such as: the use of spring in corrosive media, must have good corrosion resistance function. Precision instruments used in the spring, should have long-term stability and sensitivity, temperature coefficient to be low, high quality elements, after effect to be small, elastic modulus to be stable.
Large roll galvanized wire is made of low carbon steel wire rod processing, is made of low carbon steel, after drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized. Cooling and other surface treatment process processing. Large roll galvanized wire is divided into hot dip galvanized wire and cold galvanized wire (electric galvanized wire). Although galvanized galvanized wire and silver powder paint spray effect appearance is not much different. But the effect is very different, galvanized wire surface is zinc layer, good adhesion, good corrosion resistance.
In the process of composite electroplating galvanized wire, the plating solution must be stirred to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. The acid activation solution in the production process can remove the corrosion products and oxide film on the surface of the low carbon steel wire without excessive corrosion on the matrix.