Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Electroplating solution with solid particles or excessive foreign metal impurities, will lead to such problems. Solution: If the large roll galvanized wire to the above coating is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.
3cm electric welding net refers to the square hole net of 3cm mesh, galvanized net, impregnated plastic wire mesh, metal mesh, screen. Wide 0.914 m, 1.02 m, 1.2 m, 1.5 m, 1.8 m, length of each volume in 18 to 30 m, welded wire mesh is a wire drawing, wire with advanced welding equipment on the line of welding and become, can be cold zinc, hot dipped galvanized after welding, jinsu anticorrosive processing, also can use the black wire or change wire drawing, galvanized wire, stainless steel wire welding forming, The electric welding mesh is firm, the mesh surface is smooth, is widely used in construction, breeding, isolation, handicraft manufacturing, filtration, mechanical protection, animal fencing and other aspects, according to the demand can be customized electric welding mesh coil, can also be cut into electric welding mesh.
Secondly, the zinc-iron alloy protective layer of hot-dip galvanized wire has self-healing properties. When the surface of hot-dip galvanized wire is damaged or scratched, zinc metal can form zinc ions through electrochemical reaction, self-healing repair of the damaged zinc-iron alloy protective layer, so as to maintain the corrosion resistance of the steel wire. This self-healing property enables the hot-dip galvanized wire to be quickly repaired during use, even if there is a slight scratch or damage on the surface, avoiding further corrosion. After the ordinary steel wire is damaged on the surface, it is often unable to repair itself, which is easy to lead to the diffusion of corrosion and accelerate the aging and damage of the steel wire.
Pet cage from the use of material can be divided into plastic, wire, wire square tube, stainless steel four. General small animal cage multi-purpose is plastic and wire material, such as a lot of hamster cage, chinchilla cage are made of plastic or wire, small aquarium is plastic products, and the vast majority of small and medium-sized bird cage are wire products. The characteristics of this kind of small animal cage, is small, light, easy to carry, but also easy to clean care. For small animal cages, the wire diameter of the general iron wire is not very large, the thickness of the plastic is relatively thin, so the use of the time can not be “violent”, or the cage under the “destruction” will occur welding or plastic crack off.
The formation process of hot dip galvanized layer is between the iron matrix and the outside of the pure zinc layer, the formation of iron-zinc alloy process, the workpiece surface in hot dip plating when the formation of iron-zinc alloy layer, so that the iron and pure zinc layer is well combined. The process of large roll galvanized wire can be simply described as: when the iron workpiece is immersed in the molten zinc liquid, the first zinc and α-iron (body-centered) solid melt is formed on the interface. This is a crystal formed by the matrix metal iron dissolved with zinc atoms in the solid state. The two metal atoms are fused with each other, and the attraction between the atoms is relatively small.
Therefore, when zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms diffuse with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with zinc and sinks into the bottom of the hot-dip galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.
Any application environment, users want a better the strength of the welded wire mesh, only need to improve its intensity, will make better the habit of using demand, but to be improved in the strength of this product, also need to have the condition of many sided, just need to see factory in produce what kind of material, the strength of the product also is the material strength, But a manufacturer does not meet the strength requirements in the data, after all, there is no way to make the strength of the product progress, so this is the necessary condition.