The life of the “wire”, is actually “low carbon steel wire”, carbon content in less than 0.2%. The surface is usually coated with zinc plating because it is easy to rust. Under atmospheric conditions, the galvanized layer will not rust before most of the fall off, relatively soft. The life of the “steel wire”, is carbon content in about 0.6% of the “carbon steel wire”, or carbon content in about 0.8% of the “high carbon steel wire”, they have enough hardness and elasticity after appropriate heat treatment, high strength. Uses such as winding ordinary spring and so on.
Galvanized wire can be used zincate galvanized or chloride galvanized and other processes, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire. When the galvanized wire out of light plating should be carried out light treatment, the galvanized wire bath to control the temperature. Now the quality level of galvanized wire on the market is not equal, galvanized wire is also called hot dip zinc and hot dip galvanized, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities.
Sodium and magnesium contain less combustible impurities, and when extinguished, they simply glow. Galvanizing belongs to the electrochemical processing process which is widely used on the surface of steel. So it is, first of all, because zinc coating (especially after supplementary processing, such as chromate treatment and phosphating) resistance to atmosphere and water is more stable, and the galvanized process itself this is cheaper and simple.
Galvanized wire can be used zincate galvanized or chloride galvanized and other processes, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire. When the galvanized wire out of light plating should be carried out light treatment, the galvanized wire bath to control the temperature. Now the quality level of galvanized wire on the market is not equal, galvanized wire is also called hot dip zinc and hot dip galvanized, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities.
Excellent anticorrosive makes its popularity in the feed, the net surface smooth and tidy, increased the look and feel, can be adornment effect, this characteristic makes it to show in the mining industry, due to high quality with low carbon materials as raw materials, to make it unique general iron mesh screen does not have flexibility, determine its plasticity in use process, Thus can be used in the hardware process of deep processing and manufacturing, complex wall batch swing, underground leakage prevention cracking, light mesh body, so that the cost is much lower than the cost of iron screen, more able to understand its economic and practical.
Therefore, when zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms diffuse with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with zinc and sinks into the bottom of the hot-dip galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.
Hexagonal mesh is made of galvanized iron wire woven by automatic mesh machine, mesh into regular hexagonal shape, mesh standard, beautiful, mesh size can be customized according to customer requirements, usually 27mm,20mm, 13mm, wire diameter from 0.40mm to 1.20mm, to meet the requirements of different customers.
Cold galvanized by electrolytic action to metal and other materials surface attached to a layer of metal film, so that the surface of the material uniform texture, anti-corrosion wear, appearance is more beautiful. Hot dip galvanized coating is thicker, generally 30-60 microns, coating corrosion resistance is higher. Suitable for outdoor work of steel parts, such as highway fences, power towers, large size fasteners and other “rough” workpiece long-term rust prevention.