Steel wire and iron wire have many similarities, but carefully distinguish, will find that they are not only different in the material, but also in the product characteristics of the great difference. So when choosing, be sure to make a clear distinction between the two. Steel wire factory introduces steel wire carbon structural steel made above, generally not galvanized, used for machinery, spring. Black, very hard; Wire: made of mild steel (mild steel), galvanized, used for joining and binding. White and soft.
For the wide use of screen, the state has regulations. You also specify the diameter size, mesh size, or usage method. For plastering nets, the mesh should be less than 20 and the diameter should be greater than 1 mm. Not only are specifications specified, but safety is preferred if wire mesh is used in exterior plastering nets. If you fall, the consequences are unimaginable. Therefore, the application of norms should be combined with reality.
Field fence line net is a streamlined, streamlined, beautiful, tacky, fashionable European elegance; The diversity of color selection, a variety of standard color card colors to choose from, can meet different varieties, different, different needs. On-site fence line can be separated from a variety of methods, and according to the customer’s disagreement request.
And the role of wire mesh in the exterior wall plastering if from an Angle to sail a method of anti-falling, the role of anti-cracking is relatively small, because of the problem of orientation; And about the external insulation system is used in the tile veneer, as for the role should also be anti-drop followed by anti-cracking, so the grid should be selected 10×10×0.6, these are some experience selection, grid conversion from the national provisions of the wire mesh standard, choose the level of steel conversion.
There is no adhesion test of powder spraying or fluorocarbon spraying on packaged galvanized wire, but there are two points for reference: first, in sealed or air-free environment, non-metallic volatiles can corrode zinc coating; Second, zinc at higher than 230 degrees (c) will cause the matrix metal brittle. And powder spraying and fluorocarbon spraying are to be baked at a higher temperature and in a sealed environment, causing rapid corrosion of zinc, resulting in loose corrosion film resulting in coating adhesion decline, and even lead to (matrix) steel wire brittle situation may exist.
Cold galvanized by electrolytic action to metal and other materials surface attached to a layer of metal film, so that the surface of the material uniform texture, anti-corrosion wear, appearance is more beautiful. Hot dip galvanized coating is thicker, generally 30-60 microns, coating corrosion resistance is higher. Suitable for outdoor work of steel parts, such as highway fences, power towers, large size fasteners and other “rough” workpiece long-term rust prevention.
Large roll galvanized wire welding net is made of high quality galvanized wire welding net, wire through the current, after mutual melting, strong connection point, and the formation of metal mesh. In the use of galvanized iron wire to find the thickness and soft and hard to the size of flowers, weight and softness corresponding to the degree, too soft florets to use fine wire, and heavy flowers, flowers with thick stems to use thick wire.
Cold galvanizing (galvanizing) is in the plating tank after the current unidirectional, so that the zinc gradually plated on the metal surface, slow production speed, uniform coating, thin thickness, usually as long as 3-15g, bright appearance, poor corrosion resistance, usually a few months will rust. Compared with hot dip galvanizing, the production cost of electric galvanizing is lower.
The wire rod should be normalized or soxhlet processed, instead of spheroidal annealing for standard large ones. Soxhlet process is widely used in the heat treatment of the center, especially the products before drawing. Avoid decarbonization during heat treatment. After heat treatment, sulfuric acid or hydrochloric acid pickling is used to remove iron sheet. The coating (see smooth carrier) can be dip-lime, phosphating, borax treatment or copper plating.
Hot dip galvanizing is a kind of external treatment technology in the production of fasteners. The common varieties of hot dip galvanizing fasteners are electric galvanizing, powder galvanizing, mechanical galvanizing and hot dip galvanizing. Wire factory according to different requirements of customers for fasteners, different hot-dip galvanized surface treatment. Galvanized layer and steel is a metallurgical connection, become a part of the steel surface, so the durability of the coating is more reliable.
Generally speaking, in dry main gas and indoor use, the thickness of galvanized coating is only 6-12μm, but under poor environmental conditions, the thickness of galvanized coating is 20μm, can reach 50μm. Therefore, environmental factors should be considered when choosing the thickness of galvanized layer. Galvanized layer after passivation treatment, can naturally form a layer of bright, beautiful color passivation film, can obviously improve its protective function, decorative.