The material of steel structure will affect the organization and thickness of hot dip galvanized film. For example, high tension steel containing silicon, carbon content is high, easy to react with molten zinc quickly, the result of excessive growth of alloying, will cause a grayish black appearance, but does not affect its corrosion resistance. Or heat treated steel, if its tensile strength exceeds 90kg/mm2, after hot dip operation, easy to reduce its strength, etc.
Hot dip galvanized coating is also relatively thick, but there is an uneven situation, for example, the thickness of the thin is only 45 microns, thick can reach 300 microns or even thicker, the color of this product is relatively dark. There is also a lot of zinc consumed in the production process. Zinc will form an infiltration layer with the metal. Its advantage is that it has good corrosion resistance. Electrogalvanizing, it is through the plating tank in the zinc one-way plating on the outside of the metal products, this way of making products is relatively slow, but its thickness is more uniform.
And high quality data and production cost and production conditions are bound, so some welding screen manufacturers did not meet the requirements of this aspect, natural in this case there is no way to improve product strength. In addition to data, and produce process, even if again good data, but the factory did not meet the requirements of production process in welding, also can form the product under the high pressure welding, so it is also a kind of strength on the decline, process conditions of different manufacturers also have very big difference, so it formed a shopping mall on the above products are differences of strength.
2) wire spacing: we all know that the smaller the wire spacing, the stronger the cage, in fact, too close is not good, too close to the dog will have a feeling of repression, we recommend that you buy wire spacing between 15-25mm, so it is not too close, and not too loose.
Barbed wire is used to make barbed wire, in part, to prevent livestock theft, because the surface is covered with sharp spikes that make it very difficult to penetrate through the barbed wire. On the other hand, it is because livestock generally have the habit of charging, and the barbed rope is used to circle, which makes livestock dare not rush to charge the barbed rope, thus saving the user’s use cost.
The external environment has great influence on the preservation of galvanized wire mesh. In the rainy season, it is necessary to pay attention to the air humidity of the workshop, warehouse and other departments. It is recommended to use a humidifier. Usually, the moisture absorption of book paper is larger than that of powder paper, and the pH value is higher. Generally speaking, in the normal environment of storage wire, storage time of two years is not corroded wire phenomenon. However, it should be noted that in the process of handling the iron wire, it should be handled gently to avoid the position of the coiling coil, which will cause the smooth pulling of the wire and affect the production.
Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.
The iron wire used for the barbed wire is woven or welded into low carbon steel wire, medium carbon steel wire, high carbon steel wire, stainless steel wire and other materials. Production process: general braided, embossed braided and spot welding. If the material is steel wire, after equipment processing into a network, it is called wire mesh.
Regular maintenance and maintenance, save a lot of time, but also save the cost of maintenance and maintenance. With good stability, good corrosion resistance, greatly prolong the service life. More kinds, can be selected according to different uses, making annealing wire device is simple, improve the utilization rate of the device.
With the development of mining industry, pig iron classification in Our country has been very extensive, can satisfy the demand of machinery industry. In general, iron used to produce large coils of galvanized wire can be divided into two classes. A metal produced directly from iron ore and iron smelting, consisting of iron oxide, silicon dioxide, and other miscellaneous stones. When this ore is specially refined into metal iron, carbon, silicon, manganese, and other elements are mixed in, so that the refined material is called general pig iron, is also for the initial grade of the material.
Large roll galvanized wire is processed from high quality low carbon steel wire rod. Each wire rod rolled by continuous rolling mill is not less than 200kg, but 15% of the number of plates in each batch is allowed to be composed of two, of which the weight of each rod is not less than 80kg, and 4% of the number of plates in each batch is allowed, and the mass of its single wire rod is less than 200kg, but not less than 40kg. Each rod rolled by semicontinuous mill shall not be less than 60kg, and each batch shall be allowed to have 5% disk nitrogen. The mass of the rod shall not be less than 60kg, but not less than 30kg.
Application range of hot dip galvanizing: because of the thicker coating, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the agricultural field such as irrigation, greenhouse and construction such as water and gas transmission, wire casing, scaffolding, Bridges, road guardrail and other aspects, has been widely used.