In the process of composite electroplating galvanized wire, the plating solution must be stirred to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. The acid activation solution in the production process can remove the corrosion products and oxide film on the surface of the low carbon steel wire without excessive corrosion on the matrix.
Our country industry chooses the low carbon steel with good quality as raw material, and then produces the quality galvanized iron wire by drawing, galvanizing and other processes. Now the production technology of galvanized iron wire products can be divided into hot plating and electroplating two kinds of methods. No matter which one is chosen, it should be carried out in accordance with the corresponding operating specifications, so as to better ensure the production of good products. For key and important parts with tensile strength greater than 1034mpa before plating, the stress should be released at 200±10℃ for more than 1 hour and 140±10℃ before plating.
The custom application of hexagonal guardrail network plays a very important role in the channel slope protection work. According to the performance of the network, it can firmly grasp the soil so that it will not be lost, so the customized slope protection effect of hexagonal guardrail network is very significant, but also because of this advantage, it is widely used in such as channel protection, river bank protection, landslide protection. The custom structure of hexagonal guardrail is tightly combined, the appearance is not concave and convex, and it has satisfactory anti-corrosion, anti-oxygen and other capabilities. Construction without a lot of manpower and material resources, can be in the field of actual operation.
Secondly, the zinc-iron alloy protective layer of hot-dip galvanized wire has self-healing properties. When the surface of hot-dip galvanized wire is damaged or scratched, zinc metal can form zinc ions through electrochemical reaction, self-healing repair of the damaged zinc-iron alloy protective layer, so as to maintain the corrosion resistance of the steel wire. This self-healing property enables the hot-dip galvanized wire to be quickly repaired during use, even if there is a slight scratch or damage on the surface, avoiding further corrosion. After the ordinary steel wire is damaged on the surface, it is often unable to repair itself, which is easy to lead to the diffusion of corrosion and accelerate the aging and damage of the steel wire.
Sodium and magnesium contain less combustible impurities, and when extinguished, they simply glow. Galvanizing belongs to the electrochemical processing process which is widely used on the surface of steel. So it is, first of all, because zinc coating (especially after supplementary processing, such as chromate treatment and phosphating) resistance to atmosphere and water is more stable, and the galvanized process itself this is cheaper and simple.
Out-of-line annealing means that the recrystallization annealing of hot or cold rolled steel plate is carried out in the bottom type annealing furnace or cover type annealing furnace before entering the hot plating wire line, so that there is no annealing process in the galvanized line. The steel plate must maintain a clean active surface of pure iron, free of oxides and other dirt, before hot dip galvanizing. In this method, the annealed surface oxide sheet is first removed by pickling method, and then coated with a layer of zinc chloride or a mixture of ammonium chloride and zinc chloride solvent for protection, so as to prevent the plate from being oxidized again.
Because the large volume of galvanized wire alloy elements in iron ore, can make the copper through the material thickening degree of strengthening, hardness, impact force, strength resistance, closing rate, elongation, so alloy iron in the exercise of good iron, is an important supplementary element. The difference between galvanized wire and general iron wire is very big, general iron wire is cheap, and because iron is not very stable, easy to rust in wet places, so the stability is not very good, life is not very long.
Hexagonal guardrail network custom corrosion lost the original characteristics, in the shape, color and mechanical properties will change, resulting in equipment damage, pipeline leakage, etc., specifically, it is easy to break, lose the original protection function.