There is also in the use of places, blade thorn rope is generally installed and used for the border, walls, prisons and so on, and galvanized thorn rope is in the orchard, fence livestock and so on a large area of installation, although the use of large, but not as high as the use of blade thorn rope and grade, so this is the main reason for the high price. Finally, for the blade barbed wire, the general installation site has high requirements for the protection level, so the quality of the product is also relatively high. But the ordinary galvanized barbed wire has relatively low requirements for the quality in the processing process due to the casual requirements at the installation site.
Cold drawing wire is a metal cold processing, with wire rod as raw material, that is, the mouth of the steel bar. Cold drawing wire is a product produced by a series of processes such as shell stripping, which is a common wire. In the development and production of metal materials, cold drawing wire is a very common material, its performance is good, the range of use is very wide, manufacturers in processing are the use of cold processing to produce.
Hot dip galvanizing, also known as hot dip zinc and hot dip galvanizing, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into the molten zinc liquid at about 500℃, so that the surface of the steel member is attached with zinc layer, so as to play the purpose of anticorrosion.
The application of barbed rope is calculated in accordance with the length, but the purchase of barbed rope is calculated in accordance with the weight of the barbed rope, which causes the user is difficult to count the number of procurement confusion, so we need to understand clearly, a kilogram of barbed rope to less meters? How much does a meter of barbed rope weigh? These two problems, the procurement of thorn rope becomes very simple.
If the surface of galvanized wire is black and the galvanized layer is thin and uneven, the galvanized wire is partly because the inventory storage time is longer, but also because the production technical requirements of galvanized wire do not meet the standard and lead to the quality problems of galvanized wire. According to the use of galvanized wire is different, galvanized wire has soft and hard, then the galvanized wire used for binding requires the flexibility of galvanized wire is better, the flexibility of galvanized wire is good, and it can be easy for workers to operate.
The large roll of galvanized silk should be coated with oil, the fiber core is dipped in oil, and the grease should be able to protect the fiber core from decay and corrosion, the iron wire moistens the fiber, and lubricates the wire rope from the inside. The surface is coated with oil so that all the wire surface in the rope strand is evenly coated with a layer of anti-rust lubricating grease, which is used for the mine rope with friction lifting and mineral water, to be coated with black grease with increased wear and strong water resistance. Other uses are coated with red oil oil with strong film and good rust resistance, and require it to have a thin oil layer, which is easy to keep clean during the operation.
Carbon spring steel wire should have high tensile strength, elastic limit, endurance and fatigue strength, and impact and vibration resistance. To ensure the strength and endurance index, especially to avoid changing the occurrence of cracks, is the key to produce spring steel wire. The inner quality and surface quality of the wire rod directly affect the function of the wire.
Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, Softness is also very uniform, color is also consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding coat hanger, reprocessing industry and so on.
There are three methods to detect the thickness of zinc layer of galvanized wire: weighing method, cross section microscopy method and magnetic method, among which the first two experiments will cause certain damage to galvanized wire, including the length of galvanized wire and the reduction of dosage. The general detection of galvanized wire galvanized layer is detected by magnetic method, which is also a more intuitive and convenient method. The standard of galvanized layer thickness is related to the wire diameter of galvanized wire. The larger the wire diameter of galvanized wire, the thicker the galvanized layer is. It is the thickness of galvanized layer and cast iron after centrifugal separation.
Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.