Galvanized wire is divided into hot galvanized wire and cold galvanized wire (electric galvanized wire). Hot dip galvanizing is dipped in zinc liquid melted by heating. It has fast production speed, thick but uneven coating. The market thickness is 45g and can reach more than 300g. The color is dark, the zinc metal is consumed, and the matrix metal is formed into the entry layer, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can adhere to decades.
Large rolls of galvanized silk play a very important role in our life. Made of low carbon steel rod processing, after drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized. Cooling and other process processes. Galvanized wire is divided into hot galvanized wire and cold galvanized wire (electric galvanized wire). Galvanized iron wire has good toughness and elasticity, the amount of zinc can reach 300 g/square meter. It has the characteristics of thick galvanized layer and strong corrosion resistance.
Large coil galvanized wire in the zinc immersion distance debugging, keep the original speed unchanged, according to t= KD to determine the zinc immersion time (1), where: t is the zinc immersion time is constant, take 4-7D is the diameter of steel wire mm, and then estimate the zinc immersion distance. By adjusting the zinc dip distance, the zinc dip time of steel wire of various specifications can be shortened by 5s on average. In this way, the zinc consumption per ton of steel wire decreases from 61kg to 59.4kg.
Like highway guardrail, silk screen can be used, in production can also be according to the needs of customers, such as the need for different diameters of galvanized wire products, in the material selection and coating to carry out reasonable control. Our industry is a low carbon steel with good quality as raw material, and then through the pulling out, galvanized process, thus producing good galvanized iron wire.
Large hexagonal mesh called stone cage net, is mainly used for mountain protection, hydraulic construction and so on. Small wire hexagonal mesh is used as a good material for breeding, will twist twist hexagonal mesh in the welded iron frame on the hexagonal mesh welding into chicken coop, pigeon cage, rabbit cage cage cage, hexagonal mesh is the best material for breeding with a net.
At present, there are two processing methods of blade stabbing rope. One is to make it into a spiral shape, and then make a clip treatment. It is not only our common spiral blade stabbing rope, but also a single spiral blade stabbing rope without clip, but even a single helix can not stretch it to a relatively straight. This is mainly because the blade barbed rope is wrapped and wound at the same time, so it can only be spiral.
With a large pickpocket used for steel wire, into the zinc liquid before the surface of the zinc ash stirring; Use a small outlet for galvanized steel wire; Zinc pot steel wire outlet in 30 minutes, with pickpockets back and forth, until the large, floating zinc residue into brown, real zinc ash, zinc ash surface. The extracted zinc ash should be brown yellow real zinc ash, zinc surface, effectively reduce zinc consumption. This is one of the biggest steps to bring zinc consumption down, and it’s a real problem, one that hasn’t been solved for years.
One is the frame isolation net, guardrail net with frame, frame using material cold plate belt welded into the square tube, usually 2*3 thickness 1.2 thick, the middle for low carbon steel wire welding mesh, wire diameter can choose another welding aperture can also choose, for example, customers want good quality long service time, you can choose thick wire diameter, small welding aperture, Such mesh is not only high quality, but also long service life, customized mesh and frame after welding, surface treatment to reach the customer needs of goods.
In the process of composite plating, it is necessary to stir the plating solution to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. In the process of production, the acid activation solution can remove the corrosion products and oxide film on the surface of low carbon steel wire without excessive corrosion on the matrix. Galvanized wire can be used zincate galvanized or chloride galvanized and other processes, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire.