The anticorrosion of these raw materials is very different, and the use of life is not the same. Niu LAN net cold galvanized, also known as electroplating, galvanized quantity is very little, rust in rain, but the price is cheap, the use of life in 5-6 years. Hot dip galvanizing (low zinc and high zinc) on the amount of zinc in 60 grams to 400 grams, the service life is about 20-60 years, corrosion resistance is general.
The iron is clean and clean, and then solvent treatment, after drying immersed in zinc liquid, iron and molten zinc reaction to produce an alloyed zinc layer, the process is: degreasing – washing – pickling – assisted plating – drying – hot dip galvanizing – separation – cooling passivation. The thickness of the alloy layer of hot plating wire mainly depends on the chemical composition of the steel silicon content, the size of the steel cross-sectional area, the roughness of the steel surface, the temperature of the zinc pot, the time of dipping zinc, cooling speed, cold rolling deformation, etc.
When the coating of large galvanized wire is blistered in the process of galvanizing, the bath temperature should be checked first. If the bath temperature is not low, and then strengthen the removal of oil before plating, to prevent the base metal in acid corrosion. If you pay attention to these problems, the bubbling phenomenon still exists, it should pay attention to the dosage and quality of additives, then you can stop adding additives, with high current electrolysis for a period of time, to reduce the content of additives, observe whether the bubbling phenomenon is improved. If there is no improvement, check whether the additive has been stored for too long or whether it contains too many impurities.
3, with oil cloth (oil used cloth), carefully from inside to outside, including each cage wire repeatedly grinding many times. The front of the bird cage, the door flowers, where vision is often in place, are repeatedly rubbed in order to improve the surface finish, equivalent to “grinding”. Note: door flowers, arhat lines and other structures are delicate and fragile, do not break. This process, which requires time and patience, care, is also a process of observing and appreciating the cage. Use new cloth again, according to the above process, wipe again and again. This process is equivalent to polishing. For important parts, you can use a little force, the speed can be a little faster (do not use force). Be careful to fold the cloth neatly, otherwise marks will easily form. When this process is complete, the surface finish is significantly improved.
Paint on the galvanized layer, the binding force between each other and the baking temperature of the paint has a great relationship, after galvanized coating alkyd paint, adhesion is no problem. Galvanized amino paint, paint adhesion is not good. Do two bottom two surface, adhesion is ok, if the two bottom two surface to two bottom three surface, that is, more paint, more baking once, again test adhesion is very poor, poor to the paint from the galvanized layer of pieces torn off.
Wire mesh welding after galvanized is through the end of the welding and then the cold company to make wire mesh wire mesh steel mesh construction mesh floor heating mesh galvanized or hot galvanized. After the first galvanized welding is to change the wire mesh, after the end of welding can see the welding spot; The two processes are different prices are also very different, the cost of the first plating after welding is low, the appearance is smooth, and the cost of the first welding after plating is higher, not easy to rust.