Large roll galvanized wire as a common industrial supplies in daily life, many people will use, but many of them are not standard operation. Cold galvanized wire is one of the many categories of iron wire, widely used, cold galvanized wire is a kind of galvanized iron wire products made of high quality low carbon steel wire processing, after drawing forming, pickling rust removal, high temperature annealing, hot galvanized, cooling and other processes.
The hot plating wire is made of low carbon steel wire rod, which is processed by drawing forming, pickling and rust removal, high temperature annealing, hot dip galvanizing and cooling. Galvanized iron wire has resistance and elasticity, the amount of zinc can reach 300 g/square meter, with thick galvanized layer, strong corrosion resistance and other characteristics. Widely used in construction, handicrafts, wire mesh, highway guardrail, commodity packaging and ordinary civilian and other fields.
The production process is to roll the hot metal billet into 5mm thick steel, and then put it into the wire drawing device, draw into different diameters of the line and gradually reduce the aperture of the wire drawing disk. Production process through cooling, annealing, coating and other processing technology, and then made into a variety of different specifications of galvanized wire. Galvanized wire production because of simple process, wide application, early development. Galvanized wire or steel wire is a cold working product of steel wire, and the material used is generally low carbon steel or stainless steel.
The methods to control the thickness of galvanizing are as follows: you can slow down the lifting speed of the workpiece, control the time of galvanizing as far as possible, add the appropriate amount of thinning alloy, reduce the thickness, and improve the temperature of hot-dip galvanizing. But consider the zinc pot, iron pot should not exceed 480 degrees, ceramic pot can be 530 degrees, which can reduce the time of zinc immersion.
Cold galvanized, generally speaking, do not need heating, galvanized amount is little, this galvanized parts are easy to fall off in wet environment. Hot dip galvanizing, also known as hot dip galvanizing, is to melt the zinc ingot at high temperature, put some auxiliary materials in, and then dip the metal structural parts into the galvanized groove, so that the metal members are attached to a layer of zinc layer. The advantage of hot dip galvanized is that its anticorrosion ability is strong, the adhesion and hardness of galvanized layer is better.
Large roll galvanized wire is made of low carbon steel wire rod processing, is made of low carbon steel, after drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized. Cooling and other surface treatment process processing. Large roll galvanized wire is divided into hot dip galvanized wire and cold galvanized wire (electric galvanized wire). Although galvanized galvanized wire and silver powder paint spray effect appearance is not much different. But the effect is very different, galvanized wire surface is zinc layer, good adhesion, good corrosion resistance.
Product features: strong structure, flat surface, with good corrosion resistance, oxidation resistance. The material of small hexagonal mesh is the same as that of other hexagonal mesh, which is generally made of low carbon steel wire, stainless steel wire and galvanized steel wire as raw materials by the hexagonal mesh machine.
Plastic spraying is also we often talk about electrostatic powder spraying, it is the use of electrostatic generator to make plastic powder charged, adsorption on the surface of the iron plate, and then through 180~220 DEG C baking, so that the powder melting adhesion on the metal surface, plastic spraying products are used for indoor use of the box, paint film flat or matte effect. Spray powder mainly acrylic powder, polyester powder, etc.
After annealing, iron wire will become soft, flexibility will increase, iron is a more active metal, and more active than hydrogen, so it is a good reducing agent. At room temperature, iron in the dry air is not easy to react with oxygen, sulfur, chlorine and other non-metallic elements, its production cost is lower, use and scale is wider, better protection function, so it is an important material for iron and steel parts in a strict working environment.