In the process of composite electroplating galvanized wire, the plating solution must be stirred to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. The acid activation solution in the production process can remove the corrosion products and oxide film on the surface of the low carbon steel wire without excessive corrosion on the matrix.
Electrode application range is wide, can realize a variety of materials, a variety of profiles and a variety of joint forms of welding. (1) Welding between low carbon steel, low alloy steel, medium carbon steel, alloy steel and other metal materials or dissimilar metal materials can be achieved. The weld has good comprehensive mechanical properties, and the tensile strength can reach more than 400MPa. ⑵ Can realize the welding of large plate, steel frame, plate – tube, rod – rod, tube – tube and other profiles. ⑶, can realize docking, Angle, lap, T joint and other joint forms of welding. ⑷ mainly suitable for flat welding.(5) it can surfacing the parts of wear failure, so as to obtain the surface surfacing layer with melting depth, smooth surface and excellent performance. ⑹ It can be realized that no bevel 1 ~ 6mm thick metal sheet single-side welding double-side molding.
Cold galvanizing (galvanizing) is in the plating tank after the current unidirectional, so that the zinc gradually plated on the metal surface, slow production speed, uniform coating, thin thickness, usually as long as 3-15g, bright appearance, poor corrosion resistance, usually a few months will rust. Compared with hot dip galvanizing, the production cost of electric galvanizing is lower.
Some customers may not immediately use the blade barbed rope when they buy it for retail and some are temporarily not used for site construction. At this time, customers need to follow up the characteristics of the blade barbed rope for storage. Because they are afraid of the rain, so there is no need to say more, and the surface of the packaging is more afraid of the sun, so it is not recommended to prevent the outside of the blade thorn rope will lead to the woven bag become lost effect, resulting in the exposure of the internal blade thorn rope affect the later use.
Hot dip galvanized iron wire using high quality carbon structural steel, after drawing, galvanized iron wire processing. Hot dip galvanized iron wire is widely used in wire mesh, highway guardrail and construction projects. It has the characteristics of thick coating, strong corrosion resistance and strong coating. And according to the special needs of users, according to industry standards to provide various specifications of galvanized wire.
Spring wire shall have high tensile strength, elastic limit, endurance and fatigue strength, and be resistant to shock and oscillation. The objectives of strength and endurance, especially the prevention of alteration cracks, are key to the consumption of spring steel wires. The inner and outer quality of wire rod directly affect the function of steel wire.
Immersed six edge barbed wire corrosion lost the original characteristics, in the shape, color and mechanical properties and other aspects will change, resulting in equipment damage, pipeline leakage, specifically, is prone to fracture, lose the original protection function. Corrosion usually metal corrosion has three types: physical, chemical corrosion and electrochemical corrosion, and corrosion depends on the chemistry of the metal itself and the organizational structure, still have relationship with the surrounding medium, such as wet environment than dry environment is easy to rust, more less than the impurities of impurities is easy corrosion, high temperature conditions than under the condition of low temperature corrosion, etc. After understanding these, we can effectively prevent the corrosion of the six sides of the wire, prolong the service life of the product.