In general, the hardness of a metal is often considered to be the resistance of the material to plastic deformation, scratches, wear, or cutting. In the debugging of zinc wire dipping distance, keep the original speed unchanged, according to the time of dipping zinc, the diameter of steel wire, and then estimate the dipping distance. By adjusting the zinc immersion distance, the zinc immersion time of steel wire of various specifications is shortened by 5s on average compared with that before debugging, so that the zinc consumption per ton of steel wire is reduced from 61kg to 59.4kg.
And high quality data and production cost and production conditions are bound, so some welding screen manufacturers did not meet the requirements of this aspect, natural in this case there is no way to improve product strength. In addition to data, and produce process, even if again good data, but the factory did not meet the requirements of production process in welding, also can form the product under the high pressure welding, so it is also a kind of strength on the decline, process conditions of different manufacturers also have very big difference, so it formed a shopping mall on the above products are differences of strength.
Application range of hot dip galvanizing: because of the thicker coating, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the agricultural field such as irrigation, greenhouse and construction such as water and gas transmission, wire casing, scaffolding, Bridges, road guardrail and other aspects, has been widely used.
The material of the blade can be roughly divided into high quality steel wire, galvanized steel plate, stainless steel plate. The general technology used on the blade: hot dip galvanizing – stamping. The blade has the advantages of corrosion resistance, aging resistance, good weather resistance, easy installation, low price and so on. The use of blade rope: Blade rope has been widely used in military sites, prisons, government, banks, residences, private homes, villas, doors and Windows, roads, railway fences and border lines, etc., to ensure safety. Most prisons basically use razor blades.
For the specification of galvanized wire, the galvanized wire produced by our factory can range from No.8 to No.22, which refers to the BWG standard, that is, from about 4mm to 0.7mm, which can basically cover the type required by the customer. As for the raw material of galvanized wire, normally, we use Q195 mild steel, and some factories will also use SAE1006 or SAE1008. The following is the zinc coating, for galvanized wire, this is very important, the general zinc coating is about 50g/m2 to 80g/m2, some customers need high zinc galvanized wire, zinc coating can reach 200g/m2 to 360g/m2. The tensile strength of galvanized wire is usually 350n/m2 to 800n/m2. Then there is the packaging specification of galvanized wire. The specifications of small rolls of galvanized wire are 50kg/ roll, 100kg/ roll and 200kg/ roll. Of course, there are large rolls of galvanized wire, the weight can reach 300kg/ roll or 800kg/ roll.
Galvanized hexagonal net features: easy to use; Save transportation costs. It can be reduced to small rolls and wrapped in moisture-proof paper packaging, taking up less space. Coating thickness uniformity, stronger corrosion resistance; Simple construction, no need for special technology; It has strong ability to resist natural damage, corrosion resistance and adverse weather effects; Can withstand a large range of deformation, but still does not collapse. Fixed heat preservation and heat insulation effect.
Electro galvanizing shaft wire direct is in the electroplating tank through the current unidirectional zinc gradually plated on the metal surface, production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust. Compared with hot dip galvanizing, electric galvanizing has lower production cost. The difference between cold galvanizing and hot galvanizing: the difference between cold galvanizing and hot galvanizing is that the amount of zinc is different. They can be identified from the color. The color of cold galvanizing is shiny silver white with yellow. Hot dip galvanized shiny hair white.
What kind of wire mesh fence should be used for chickens, ducks, geese and other light poultry? The so-called good refers to the high cost performance, that is, the use effect can be achieved, such as the size of the mesh, the size, etc., and the cost can be reduced to the greatest extent.