The hot plating wire uses zinc-free slag to add hot melt zinc and galvanize, which avoids the traditional heating process and radiates the surface 1653 of zinc liquid surface 4102 to the hot melt zinc, reducing the high temperature oxidation on the surface of zinc liquid. At the same time, the heating body is in contact with the zinc liquid, and the heat is directly transferred to the zinc liquid. The utilization rate of heat energy can reach more than 90%, which reduces the heat radiation of the zinc liquid surface.
The impregnated hexagonal wire mesh will lose its original characteristics after corrosion, and will change in shape, color and mechanical properties, resulting in equipment damage, pipeline leakage, etc., specifically, it is easy to break and lose the original protection function. Usually there are three kinds of metal corrosion: physical corrosion, chemical corrosion, electrochemical corrosion, corrosion in addition to the chemical properties and organizational structure of the metal itself, but also related to the surrounding medium, such as wet environment than dry environment easy corrosion, more impurities than impurities less easy corrosion, high temperature conditions than low temperature conditions easy corrosion. After understanding these, we can effectively prevent the corrosion of impregnated hexagonal wire mesh, prolong the service life of products.
After passivation treatment of galvanized layer, a layer of bright old and beautiful color passivation film can be generated, which can significantly improve its protective performance. There are many kinds of galvanized solution, which can be divided into cyanide plating solution and cyanide plating solution. Cyanide galvanizing solution has good dispersion and covering ability, coating crystallization is smooth and fine, simple operation, wide application range, has been used in production for a long time.
What’s the difference between cold galvanized wire and hot galvanized wire? It is mainly different production process. Cold galvanized iron wire, also known as electric galvanized iron wire, is the use of electrolytic galvanizing process, and hot galvanized iron wire is the use of hot penetration galvanizing process. Compared with the two, hot dip galvanized iron wire thick coating, high zinc content, has stronger anti-corrosion and anti-rust effect. Similarly, the price is also higher, cold galvanized iron wire and hot galvanized iron wire which good? Mainly for the use of scenarios and requirements to choose appropriate galvanized iron wire, appropriate is better.
There is no need to carry out daily maintenance and maintenance when in use, which can not only save a lot of time, but also reduce the cost, but also has good stability, strong corrosion resistance, greatly extend the service life. According to the different technology is divided into different types, can be selected according to their own needs, has better flexibility and elasticity. The main function of annealing wire is to control its hardness, when the annealing wire is made of steel wire.
Galvanized wire in acid, alkali, sodium chloride aqueous solution of poor corrosion resistance, in the atmosphere containing carbon dioxide and hydrogen sulfide, as well as Marine atmosphere is not corrosion resistance. In high temperature and high humidity air and containing organic acid atmosphere is small, galvanized layer is also easy to be corroded. Galvanized wire and general wire is very different, general wire is cheap, and because the iron is not very stable, easy to rust in the wet place, so the stability is not very good, the life is not very long.