Large roll galvanized wire is processed from high quality low carbon steel wire rod. Each wire rod rolled by continuous rolling mill is not less than 200kg, but 15% of the number of plates in each batch is allowed to be composed of two, of which the weight of each rod is not less than 80kg, and 4% of the number of plates in each batch is allowed, and the mass of its single wire rod is less than 200kg, but not less than 40kg. Each rod rolled by semicontinuous mill shall not be less than 60kg, and each batch shall be allowed to have 5% disk nitrogen. The mass of the rod shall not be less than 60kg, but not less than 30kg.
Different from the general zinc barbed rope, the zinc content of the surface of the high zinc barbed rope is very high, which can reach 6-8 times of the former, so that it has a great advantage in service life. Ordinary products begin to corrosion in three or five years, while the latter takes longer time to change. Stainless steel barbed rope is in the material aspect of protection so durability is also better, these two products are known for long service life, but is high in price.
The quality of hot-dip galvanized barbed wire is only in the surface of the wire attached to the galvanized layer, and with the reason of the chemical reaction, the surface of the zinc layer will gradually lose its role because of the oxidation reaction, this situation is more prominent in humid areas. And because after all, the steel wire will rust, so the quality of hot-dip galvanized barbed wire is certainly not up to the level of stainless steel barbed wire.
Cold galvanizing (galvanizing) is in the plating tank after the current unidirectional, so that the zinc gradually plated on the metal surface, slow production speed, uniform coating, thin thickness, usually as long as 3-15g, bright appearance, poor corrosion resistance, usually a few months will rust. Compared with hot dip galvanizing, the production cost of electric galvanizing is lower.
Specific requirements for the safety of galvanized wire production: clean up all tools and other objects that hinder production in the galvanized wire production environment. Operators in the pickling process, pay attention to the action should be careful, not careless, into the pickling tank must be handled lightly, to prevent splashing on the body. When adding acid, the acid must be slowly poured into the water. It is forbidden to pour the water into the acid, so as to prevent the acid from splashing out and hurting people. Do not hurt yourself or others.
The height of the shield should not be less than two meters. The length of the shield should be the width of the journey and the extension 10 meters away. The vertical load of the handrail on the bridge is 1.2KM/m, and the horizontal external load is 2.5KM/m, both of which should be calculated separately. Galvanized hook mesh is attributed to a hook mesh, it is the selection of galvanized wire, hot dip galvanized wire as raw materials, woven through the hook mesh crimping truncated.
There is no adhesion test of powder spraying or fluorocarbon spraying on packaged galvanized wire, but there are two points for reference: first, in sealed or air-free environment, non-metallic volatiles can corrode zinc coating; Second, zinc at higher than 230 degrees (c) will cause the matrix metal brittle. And powder spraying and fluorocarbon spraying are to be baked at a higher temperature and in a sealed environment, causing rapid corrosion of zinc, resulting in loose corrosion film resulting in coating adhesion decline, and even lead to (matrix) steel wire brittle situation may exist.
After the corrosion of impregnated hexagonal wire mesh, the original characteristics will be lost, and the shape, color and mechanical properties will be changed, resulting in equipment damage, pipeline leakage, etc., specifically, it is easy to break and lose the original protection function. Usually, there are three kinds of metal corrosion: physical corrosion, chemical corrosion, electrochemical corrosion, corrosion in addition to the chemical properties and organizational structure of the metal itself, but also related to the surrounding medium, such as wet environment is easier to rust than dry environment, more impurities than impurities less easy corrosion, high temperature conditions than low temperature conditions easy corrosion. After understanding these, we can effectively prevent the corrosion of impregnated six-sided wire mesh, prolong the service life of the product.
Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Solid particles or excessive foreign metal impurities in the electroplating solution can cause such problems. Solution: If the coating of large galvanized wire is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.
Large roll galvanized wire is divided into hot dip galvanized and cold galvanized two kinds, hot dip galvanized color is dark, consumption of zinc metal, and matrix metal formation of infiltration layer, good corrosion resistance, hot dip galvanized can be maintained for decades in outdoor environment. Cold galvanized production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust.
1, no paint and maintenance, long new not old, exempt you from maintenance fatigue and trouble, the lowest comprehensive cost. Stainless steel wire mesh can be used as poultry cage, egg basket, channel fence, drain tank, porch guardrail, anti rat net, mechanical protective cover, livestock and plant fence, grid frame, etc.