The hot plating wire is made of low carbon steel wire rod, which is processed by drawing forming, pickling and rust removal, high temperature annealing, hot dip galvanizing and cooling. Galvanized iron wire has resistance and elasticity, the amount of zinc can reach 300 g/square meter, with thick galvanized layer, strong corrosion resistance and other characteristics. Widely used in construction, handicrafts, wire mesh, highway guardrail, commodity packaging and ordinary civilian and other fields.
Heavy hexagonal mesh is made of steel wire woven into hexagonal mesh by special machinery. This kind of mesh, after cutting and assembling, can be made into fence mesh, mountain hanging mesh, vegetation three-dimensional mesh, assembly, etc. Alias: gabion mesh, heavy hexagonal mesh, ecological mesh, wire mesh, etc.
Electro galvanizing shaft wire direct is in the electroplating tank through the current unidirectional zinc gradually plated on the metal surface, production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust. Compared with hot dip galvanizing, electric galvanizing has lower production cost. The difference between cold galvanizing and hot galvanizing: the difference between cold galvanizing and hot galvanizing is that the amount of zinc is different. They can be identified from the color. The color of cold galvanizing is shiny silver white with yellow. Hot dip galvanized shiny hair white.
The physical methods mainly include manual rust removal and mechanical rust removal, chemical rust removal is generally the use of pickling method, practical application, usually according to the appearance of the workpiece rust status and different post-treatment process, choose different rust removal methods, among which pickling rust cleaning is more commonly used. That is, the iron and steel workpiece with oxide skin or rust is etched in the acid lotion, mainly to remove the oxide or rust layer on the surface of the steel.
Therefore, when zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms diffuse with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with zinc and sinks into the bottom of the hot-dip galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.
Every time galvanized wire production enters the peak season of the industry, the road leading to the factory will see from time to time transport wire and container vehicles, as well as galvanized bright wire short-distance transport trucks, driving the labor utilization rate in the surrounding countryside, solving the employment problem of most people. Galvanized wire is divided into hot dip galvanized wire and cold galvanized wire difference: hot dip galvanized is in the heated melting zinc liquid dip plating, production speed is fast, the coating is thick but not uniform. Dark color, consumption of zinc metal, and matrix metal formation of infiltration layer, good corrosion resistance, hot dip galvanizing in outdoor environment can be maintained for decades.
Large hexagonal net called stone cage net, stone cage net before delivery, must be folded into a simple surface, packed compression after delivery. Then put it into the right position to open, and then put the appropriate size of the stone into the cage, the lid tight, and then the various stone cage net and adjacent stone cage net tied up.