Bridge protection system generally do not need to be specially installed special drainage system, the use of hexagonal mesh made of gabion mesh box, the inside of the filler are selected stones, these stones are not easy to wear, and between the stones and stones will retain some gaps, so it is very good to meet the drainage requirements.
4, safety, environmental protection, harmless to people (livestock), even if it does not intend to touch the guardrail will not hurt like steel, iron guardrail. Stainless steel wire mesh can be used as poultry cage, egg basket, channel fence, drain tank, porch guardrail, anti rat net, mechanical protective cover, livestock and plant fence, grid frame, etc.
Razor wire, also known as razor wire and razor net, is a new type of protective net. Blade barbed wire has beautiful, economic and practical, good anti-resistance effect, convenient construction and other excellent characteristics, at present, blade barbed wire has been widely used in many countries of industrial and mining enterprises, garden apartments, border posts, military fields, prisons, detention houses, government buildings and other countries of the security facilities.
The hot plating wire uses zinc-free slag to add hot melt zinc and galvanize, which avoids the traditional heating process and radiates the surface 1653 of zinc liquid surface 4102 to the hot melt zinc, reducing the high temperature oxidation on the surface of zinc liquid. At the same time, the heating body is in contact with the zinc liquid, and the heat is directly transferred to the zinc liquid. The utilization rate of heat energy can reach more than 90%, which reduces the heat radiation of the zinc liquid surface.
Hot dip galvanizing, also known as hot dip galvanizing, is a method of obtaining a metal covering layer by immersing a steel member into a molten zinc solution. With the rapid development of high-voltage power transmission, transportation and communication, the protection requirements for steel parts are becoming higher and higher, and the demand for hot-dip galvanizing is also increasing. Usually the thickness of electrogalvanized layer is 5 ~ 15μm, and the large roll galvanized wire layer is generally more than 35μm, or even up to 200μm. Hot dip galvanized coating ability is good, dense coating, no organic inclusions.
After the corrosion of impregnated hexagonal wire mesh, the original characteristics will be lost, and the shape, color and mechanical properties will be changed, resulting in equipment damage, pipeline leakage, etc., specifically, it is easy to break and lose the original protection function. Usually, there are three kinds of metal corrosion: physical corrosion, chemical corrosion, electrochemical corrosion, corrosion in addition to the chemical properties and organizational structure of the metal itself, but also related to the surrounding medium, such as wet environment is easier to rust than dry environment, more impurities than impurities less easy corrosion, high temperature conditions than low temperature conditions easy corrosion. After understanding these, we can effectively prevent the corrosion of impregnated six-sided wire mesh, prolong the service life of the product.
In view of this situation, many manufacturers are committed to ensuring the corrosion resistance of titanium and titanium alloy under the premise of increasing the hardness of titanium alloy, and surface carburizing is one of the typical processing technology means. Similar to the surface carburizing treatment of steel, the surface carburizing treatment of titanium alloy is to make the active carbon atoms, diffusion to the internal of titanium alloy, the formation of a certain thickness of higher carbon content of the carburizing layer, after quenching and tempering, so that the surface layer of the workpiece to obtain high carbon content of titanium alloy wire.
There is no adhesion test of powder spraying or fluorocarbon spraying on packaged galvanized wire, but there are two points for reference: first, in sealed or air-free environment, non-metallic volatiles can corrode zinc coating; Second, zinc at higher than 230 degrees (c) will cause the matrix metal brittle. And powder spraying and fluorocarbon spraying are to be baked at a higher temperature and in a sealed environment, causing rapid corrosion of zinc, resulting in loose corrosion film resulting in coating adhesion decline, and even lead to (matrix) steel wire brittle situation may exist.
Paint on the galvanized layer, the binding force between each other and the baking temperature of the paint has a great relationship, after galvanized coating alkyd paint, adhesion is no problem. Galvanized amino paint, paint adhesion is not good. Do two bottom two surface, adhesion is ok, if the two bottom two surface to two bottom three surface, that is, more paint, more baking once, again test adhesion is very poor, poor to the paint from the galvanized layer of pieces torn off.