When galvanized wire out of the light plating should be carried out light treatment. The bath temperature of galvanized wire should be controlled well. Galvanized wire, also known as hot dip zinc and hot dip galvanized, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into the molten zinc liquid at about 500℃, so that the surface of the steel member is attached with zinc layer, so as to play the purpose of anticorrosion.
If the surface of galvanized wire is black and the galvanized layer is thin and uneven, the galvanized wire is partly because the inventory storage time is longer, but also because the production technical requirements of galvanized wire do not meet the standard and lead to the quality problems of galvanized wire. According to the use of galvanized wire is different, galvanized wire has soft and hard, then the galvanized wire used for binding requires the flexibility of galvanized wire is better, the flexibility of galvanized wire is good, and it can be easy for workers to operate.
Razor blade barbed rope has been widely used in military sites, prisons, government agencies, banks in the world. The walls of living quarters, private homes, villas, fences, doors and Windows, highways, railway guardrail and border lines and other protection and security.
Hot wire plating adopts zinc-free slag to add hot molten zinc and galvanizing, which avoids the traditional heating process, radiates 1653 hot molten zinc on surface 4102 of zinc liquid surface, and reduces the high temperature oxidation of zinc liquid surface. At the same time, the heating body is in contact with the zinc liquid, and the heat is directly transferred to the zinc liquid. The utilization rate of heat energy can reach more than 90%, and the heat radiation on the zinc liquid surface is reduced.
In reinforced concrete structure, the crack width of cold wire drawing is smaller than that of circular steel bar or even that of hot rolled thread bar. So cold wire drawing is more popular in the construction industry. The material for cold drawing is made of steel bars and can be simply explained how it is made, that is, its production process is simple. It’s based on steel bars, which are constantly stretched evenly, stretching the bars into something very thin, like wire drawing, without plasticity.
The hot plating wire is made of low carbon steel wire rod, which is processed by drawing forming, pickling and rust removal, high temperature annealing, hot dip galvanizing and cooling. Galvanized iron wire has resistance and elasticity, the amount of zinc can reach 300 g/square meter, with thick galvanized layer, strong corrosion resistance and other characteristics. Widely used in construction, handicrafts, wire mesh, highway guardrail, commodity packaging and ordinary civilian and other fields.
We must have a certain understanding of the hexagonal network, we are the beautiful appearance of the hexagonal network, hexagonal network is not only very beautiful appearance, in fact, the practical value of survival is very high. To introduce the relevant information should be very clearly know the highway guardrail net, hexagonal wire netting in all kinds of fence netting, in the value of the high-speed on the road more MaoJian, it not only be used in all kinds of road, in a sports ball games venue and try our best to take care of landslides, also has reached very matter effectiveness.
In the calculation process of 12*14 specifications of barbed rope, it can not be calculated according to the above calculation formula, because first of all, two specifications of raw materials are used, the thinner the wire diameter, the higher the processing cost. Generally speaking, a kilogram of 12*14 barbed rope can reach about 7.5 meters, and the ratio of warp wire to barbed rope cannot be calculated according to the traditional ratio of 7 to 3. The specific use of how much wire and silk need to go through a series of professional measurement but also increase the loss of raw materials and other factors to calculate. Thorn rope factory will also according to customer needs to calculate the reasonable amount of customer use.
Good galvanized wire, plating thickness of 3- 4 mm, zinc adhesion should be less than 460 grams/m, that is, the average thickness of zinc layer is not less than 65 microns. When the thickness of plated parts is greater than 4 mm, the zinc adhesion should not be less than 610 g/m, that is, the average thickness of zinc layer should not be less than 86 microns. Standard galvanized wire coating must be uniform, galvanized layer basically uniform with copper sulfate solution test etching five times no dew iron. For standard galvanized wire coating adhesion requirements, the zinc layer of plated parts should be firmly combined with the basic metal and have enough adhesion strength, after hammer test does not fall off, not convex.
There is a connection between the hook mesh and the aperture, in short, the general hole small hook mesh, the wire is also very small; Aperture is large, hook mesh wire is generally larger. The weaving of the hook mesh also has certain rules, using the first pre-bent into a wavy wire, and then woven into the hook mesh. According to the knitting method, the hook mesh can be divided into: closed weaving, two-way plain weaving, one-way corrugated weaving, two-way plane weaving, two-way corrugated weaving, rectangular hole weaving.