The protective duration of galvanized iron wire is closely related to the thickness of galvanized iron wire. In general, zinc layer thickness needs to be very high in dry main gas and indoor applications, but in harsh environments. Therefore, in the selection of galvanized layer thickness, the impact of the environment should be considered. If galvanized iron wire products of different diameters are required, material selection and coating should be controlled reasonably.
Therefore, when the zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms are diffused with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with the iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with the zinc and sinks into the bottom of the hot galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.
The size of the dog cage is generally relatively small, suitable for indoor small dogs, dog cage is easy to carry, go out to compare the use, folding dog cage high strength steel wire and steel pipe material, the outer layer spray treatment. Strong texture, excellent rust resistance, the dog cage inside the tray, can be pulled out, convenient to clean the dog’s urine and feces, folding, dog cage is suitable for families and pet stores to raise more pet dogs.
Features: Strong flexibility, good plasticity, a wide range of uses process: selection of high-quality low-carbon raw materials, after drawing, annealing processing, soft and strong tensile resistance. The finished product is coated with anti-rust oil, not easy to rust, can be bundled according to customer requirements, each bundle is 1-50kg, can also be made into U wire, broken wire, etc., plastic inside and linen outside packaging, mainly used for binding wire, construction wire, etc.
It’s not clear why friends would want to use building nets for floor heating. What are its advantages in the floor heating project, the role of steel wire mesh is convenient for construction. Building mesh can better fix the pipe, conducive to the construction of the floor, improve efficiency. Anti crack function. The building network can improve the bearing capacity of the foundation of the thermal insulation board, the thicker the diameter of the steel wire of the building, the greater the bearing capacity, effectively prevent the appearance of cracks and cracks of steel wire mesh can improve the thermal shrinkage and contraction of cement, strengthen the tensile strength of cement, improve the quality of the heating project.
The main factors causing metal rust: relative humidity of the atmosphere at the same temperature, the percentage of water vapor content and water vapor saturation content in the atmosphere, known as relative humidity. Under certain relative humidity, the corrosion rate of metal antirust oil is very small, but higher than the relative humidity, the corrosion rate increases suddenly. This relative humidity is called the critical humidity. When the humidity in the atmosphere is higher than the critical humidity, the metal surface will appear water film or water droplets, if the atmosphere contains harmful impurities, dissolved in the water film, water droplets, electrolytes and aggravate corrosion.
Therefore, when the zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms are diffused with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with the iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with the zinc and sinks into the bottom of the hot galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.
5, the concentration of plating aid can not be too high, which is a factor that can not be ignored to reduce zinc consumption. The concentration of plating aid should not be too high. The galvanized line must be added with ammonium chloride and zinc chloride according to the data of laboratory analysis, and the specific gravity of the composite solution should be controlled within the range of 50~80g/L. If ammonium chloride or zinc chloride is arbitrarily added without the results of laboratory analysis, it should be criticized and educated, and economic treatment should be given if necessary.