It’s not clear why friends would want to use building nets for floor heating. What are its advantages in the floor heating project, the role of steel wire mesh is convenient for construction. Building mesh can better fix the pipe, conducive to the construction of the floor, improve efficiency. Anti crack function. The building network can improve the bearing capacity of the foundation of the thermal insulation board, the thicker the diameter of the steel wire of the building, the greater the bearing capacity, effectively prevent the appearance of cracks and cracks of steel wire mesh can improve the thermal shrinkage and contraction of cement, strengthen the tensile strength of cement, improve the quality of the heating project.
We must have a certain understanding of the hexagonal network, we are swayed by the beautiful shape of the hexagonal network, not only the shape of the hexagonal network is very beautiful, in fact, the practical value of survival is very high. The relevant information of Shaojie should be very clear to know that the high speed road guardrail network, hexagonal mesh of all kinds of guardrail network, the value of the high speed road is more prominent, it is not only used in a variety of roads, in a variety of sports ball venues and landslides to take care of, but also to reach a very close utility.
Hexagonal mesh is made of galvanized iron wire woven by automatic mesh machine, mesh into regular hexagonal shape, mesh standard, beautiful, mesh size can be customized according to customer requirements, usually 27mm,20mm, 13mm, wire diameter from 0.40mm to 1.20mm, to meet the requirements of different customers.
“Dry” hot dip galvanizing is also called “drying solvent method” hot dip galvanizing. Iron and steel work pieces through degreasing, pickling, cleaning, dipping aid solvent and drying, and then immersed in the molten zinc solution to galvanize. The co-solvent is usually hydrochloric acid, ammonium chloride, or ammonium chloride mixed with zinc chloride in aqueous solution.
5, the concentration of plating aid can not be too high, which is a factor that can not be ignored to reduce zinc consumption. The concentration of plating aid should not be too high. The galvanized line must be added with ammonium chloride and zinc chloride according to the data of laboratory analysis, and the specific gravity of the composite solution should be controlled within the range of 50~80g/L. If ammonium chloride or zinc chloride is arbitrarily added without the results of laboratory analysis, it should be criticized and educated, and economic treatment should be given if necessary.
The protective duration of the galvanized layer of large roll galvanized wire is closely related to the thickness of the coating. Generally speaking, in relatively dry main gas and indoor use, and in harsh environmental conditions, the thickness of galvanized layer needs to be very high. Therefore, the environmental impact should be considered when choosing the thickness of galvanized layer. After passivation treatment of galvanized layer, a layer of bright old and beautiful color passivation film can be generated, which can significantly improve its protective performance.
Steel wire after galvanized treatment, the surface will be covered with a layer of zinc metal, to play the role of anti-corrosion, anti-fouling, enhance strength and beauty. The galvanized wire drawing treatment is to process the steel wire by stretching method to obtain a finer, higher strength and smoother surface, and improve its mechanical properties. However, will wire drawing affect the electrical conductivity of galvanized steel wire?