Annealed wire is a soft iron wire made of low carbon steel cold drawing, heating, constant temperature, heat preservation and other processes. The composition of iron wire varies according to its use. It contains iron, cobalt, nickel, copper, carbon, zinc, and other elements. The hot metal billet rolled into 6.5mm thick steel bar is the wire rod, and then put it into the wire drawing device into a different diameter of the line, and gradually reduce the aperture of the wire tray, cooling, annealing, plating and other processing technology made of various specifications of iron wire.
The different spacing of the thorn rope is mainly in order to save costs to consider, because if they are too close, then obviously a little waste of resources, but the installation is too sparse will not work. Usually the bottom spacing is about 10cm, and the top is up to 20cm, this is because the higher the place is more difficult to climb over, usually more than one meter without the help of tools it is difficult for ordinary people to climb over, and the bottom because of the relatively tight can prevent personnel from drilling in the past.
Hot dip galvanized iron wire using high quality carbon structural steel, after drawing, galvanized iron wire processing. Hot dip galvanized iron wire is widely used in wire mesh, highway guardrail and construction projects. It has the characteristics of thick coating, strong corrosion resistance and strong coating. And according to the special needs of users, according to industry standards to provide various specifications of galvanized wire.
Generally, galvanized wire used for welding is required to have a certain hardness. After acceptance of galvanized wire, the first thing to do is to feel the hand, and the other thing is to test on the machine. Because the average user does not have testing equipment, it is also very inconvenient to test on the machine. Use a micrometer to measure the diameter of galvanized wire evenly, and keep it about 0.02mm above and below the contract signing standard, with neat appearance, no leakage plating and no mess.
Hot dip galvanized coating is also relatively thick, but there is an uneven situation, for example, the thickness of the thin is only 45 microns, thick can reach 300 microns or even thicker, the color of this product is relatively dark. There is also a lot of zinc consumed in the production process. Zinc will form an infiltration layer with the metal. Its advantage is that it has good corrosion resistance. Electrogalvanizing, it is through the plating tank in the zinc one-way plating on the outside of the metal products, this way of making products is relatively slow, but its thickness is more uniform.
The production process is to roll the hot metal billet into 5mm thick steel, and then put it into the wire drawing device, draw into different diameters of the line and gradually reduce the aperture of the wire drawing disk. Production process through cooling, annealing, coating and other processing technology, and then made into a variety of different specifications of galvanized wire. Galvanized wire production because of simple process, wide application, early development. Galvanized wire or steel wire is a cold working product of steel wire, and the material used is generally low carbon steel or stainless steel.
Broken wire is the iron bright wire, fire wire, galvanized wire, plastic coated wire, paint wire and other metal wire, wire factory according to customer requirements for straightening after sizing cut, has the characteristics of easy transportation, easy to use, widely used in the construction industry, handicrafts, daily civilian and other fields. No limit on length, packing as required. Annealing wire also known as black oiled wire, black annealing wire, fire wire, black iron wire. Compared with cold drawing, black annealed wire is more economical as raw material for nails.
3, with oil cloth (oil used cloth), carefully from inside to outside, including each cage wire repeatedly grinding many times. The front of the bird cage, the door flowers, where vision is often in place, are repeatedly rubbed in order to improve the surface finish, equivalent to “grinding”. Note: door flowers, arhat lines and other structures are delicate and fragile, do not break. This process, which requires time and patience, care, is also a process of observing and appreciating the cage. Use new cloth again, according to the above process, wipe again and again. This process is equivalent to polishing. For important parts, you can use a little force, the speed can be a little faster (do not use force). Be careful to fold the cloth neatly, otherwise marks will easily form. When this process is complete, the surface finish is significantly improved.