If the zinc coating is good, but when the light comes out in 3% nitric acid, there is a dark shadow on the coating, and the film is brown when passivation occurs, which may be caused by foreign metal impurities such as copper or lead in the galvanized liquid. When there is a problem in the process of galvanizing, check the temperature and current density first, and then measure and adjust the content of zinc and sodium hydroxide in the bath through the analysis of the bath. Whether DPE levels are low can be determined by Hull cell test.
The production process of large rolls of galvanized wire is a level of drawing, through the mold into a slightly smaller diameter than the original. And so on down to the desired length. One pull is not desirable, must be numbered, from coarse to fine is dependent on metal ductility. If it changes too much it just breaks. After drawing to a certain diameter, galvanized, so that the finished product.
If the surface of galvanized wire is black and the galvanized layer is thin and uneven, the galvanized wire is partly because the inventory storage time is longer, but also because the production technical requirements of galvanized wire do not meet the standard and lead to the quality problems of galvanized wire. According to the use of galvanized wire is different, galvanized wire has soft and hard, then the galvanized wire used for binding requires the flexibility of galvanized wire is better, the flexibility of galvanized wire is good, and it can be easy for workers to operate.
During this process, each time the wire is pulled over, the surface hardens due to the high friction temperature. So basically every time you pull it you have to annealing it in the furnace. On the one hand, it is to reduce the surface hardness. On the other hand, during the process of wire pulling, only the surface is deformed, and the center is unchanged. So there’s a lot of stress inside. Therefore, it is necessary to rely on annealing to eliminate the internal stress, so that the wire becomes soft again to eliminate the stress before being drawn again.
Galvanized hook mesh standard is thorough, mesh planning: 3cm-20cm, silk planning: 1.2mm-4.5mm, galvanized hook mesh 6000 square meters, some standards are available. Benefits: The selection of low carbon steel wire, surface for cold galvanized (electric galvanized) hot dip galvanized anticorrosion treatment, mesh wire strong, strong protection, long anticorrosion time.
Galvanized iron wire can be divided into hot-dip galvanized iron wire and cold galvanized iron wire according to different processing methods. Galvanized iron wire is more prominent in its corrosion resistance. Galvanized iron wire has good toughness and elasticity, the amount of zinc can reach 300 g/square meter, with thick galvanized layer, strong corrosion resistance and other characteristics. Galvanized iron wire products are widely used in construction, handicrafts, wire mesh preparation, the production of galvanized hook mesh, wall mesh, highway guardrail, product packaging and daily civilian and other fields.
Annealed wire is a soft iron wire made of low carbon steel cold drawing, heating, constant temperature, heat preservation and other processes. The composition of iron wire varies according to its use. It contains iron, cobalt, nickel, copper, carbon, zinc, and other elements. The hot metal billet rolled into 6.5mm thick steel bar is the wire rod, and then put it into the wire drawing device into a different diameter of the line, and gradually reduce the aperture of the wire tray, cooling, annealing, plating and other processing technology made of various specifications of iron wire.
The shape of the cage has round, square, octagonal, hexagonal and other shapes. Because the circular space uses a large area, it is more suitable for the activities of birds, and it is not easy to get hurt, so it is popular with everyone. A cage is dear to a man who loves birds, for it is inhabited by his master’s birds. If well maintained, it can be maintained for many years. Let’s look at how to maintain the cage.
Different from the general zinc barbed rope, the zinc content of the surface of the high zinc barbed rope is very high, which can reach 6-8 times of the former, so that it has a great advantage in service life. Ordinary products begin to corrosion in three or five years, while the latter takes longer time to change. Stainless steel barbed rope is in the material aspect of protection so durability is also better, these two products are known for long service life, but is high in price.
Generally speaking, in dry main gas and indoor use, the thickness of galvanized coating is only 6-12μm, but under poor environmental conditions, the thickness of galvanized coating is 20μm, can reach 50μm. Therefore, environmental factors should be considered when choosing the thickness of galvanized layer. Galvanized layer after passivation treatment, can naturally form a layer of bright, beautiful color passivation film, can obviously improve its protective function, decorative.
Pet cage is generally made of high quality iron wire, low carbon steel wire, stainless steel wire welding, which is characterized by beautiful, lightweight, folding, easy to store. The surface treatment of pet cage is generally: cold galvanized, hot galvanized, spray, dip, chromium plating, nickel plating and other methods.
The type of barbed rope is mainly reflected in the specification of the wire diameter, the thicker the diameter of the barbed rope produced is shorter, at the same time, the price is cheaper, mainly because the production efficiency is relatively high, because the price of the barbed rope is calculated according to the weight when it is sold. On the contrary, the finer the diameter of the wire, the longer the price is higher.