Large coil galvanized wire is made of high quality low carbon steel wire rod processing, is made of high quality low carbon steel, after drawing molding, pickling rust removal, high temperature annealing, hot dip galvanized. Cooling process and other processing. Galvanized wire is divided into hot galvanized wire and cold galvanized wire. Galvanized wire in the process of smelting there are a lot of need to pay more attention to the place, galvanized wire products in the manufacturing process will experience a lot of process, of which the following galvanized wire annealing is a very important step, this step to the nature of galvanized wire has brought a lot of help.
After passivation treatment of galvanized layer, a layer of bright old and beautiful color passivation film can be generated, which can significantly improve its protective performance. There are many kinds of galvanized solution, which can be divided into cyanide plating solution and cyanide plating solution. Cyanide galvanizing solution has good dispersion and covering ability, coating crystallization is smooth and fine, simple operation, wide application range, has been used in production for a long time.
The quantity should be the same as the contract, cold drawing, carefully record the quantity of each specification and packing method. If there is a label, check whether the label is correct and take a photo to confirm. Each roll of iron wire is fastened with galvanized packing tape, and then tied with a very strong transparent plastic bag. The coated iron wire is wrapped with white braided cloth, and the galvanized iron wire is wrapped with green braided cloth, so as to ensure that the packaging will not be lax in the transportation process.
There is no need to carry out daily maintenance and maintenance when in use, which can not only save a lot of time, but also reduce the cost, but also has good stability, strong corrosion resistance, greatly extend the service life. According to the different technology is divided into different types, can be selected according to their own needs, has better flexibility and elasticity. The main function of annealing wire is to control its hardness, when the annealing wire is made of steel wire.
Now most people want to choose a few when choosing barbed wire material better thorn rope, but the special barbed wire the better, not right, it is important to choose which model is most suited to their own thorn rope,, although is very simple product, but in the use of these products are for specific situation is different, and has a different effect, Maybe now consumers do not have too much concept of blade barbed rope, in fact, such barbed rope products have a higher safety factor.
Titanium alloy with low carbon content is obtained because the carbon content remains the original concentration. The hardness of titanium alloy is mainly related to its carbon content. Therefore, after carburizing and subsequent heat treatment, the workpiece can obtain the performance of hard and tough inside. Galvanized wire varieties are mainly classified into three categories: electric galvanized wire, hot galvanized wire and galvanized wire. Among them, the classification of galvanized wire is divided into large roll galvanized wire, medium roll galvanized wire, small roll galvanized wire, galvanized shaft wire, truncated galvanized wire and other main production varieties.
In the process of composite electroplating galvanized wire, the plating solution must be stirred to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. The acid activation solution in the production process can remove the corrosion products and oxide film on the surface of the low carbon steel wire without excessive corrosion on the matrix.
Crevice corrosion is a kind of corrosion in small area, especially in concealed position, which can form vicious corrosion cycle. Almost all the crevice corrosion can occur in a metal alloy, with gas containing active anionic neutral medium Z is easy to cause crevice corrosion, crevice corrosion often occurs in the aperture of 0.025 to 0.1 mm, because of long time gathered, the cracks will exist a series of impurities, coupled with the external environment of damp easily corrode the area of the gap is small.
Traditional wire mesh is crisscross woven into the wire, with the development of the economy, the rapid rise of all walks of life, the use of traditional wire mesh limitations gradually exposed, such as: aquaculture, to the chicken circle a cage can not be too dense, the wire can not be too thick, woven up the net wire once the mesh is too large net surface will become soft.
Traditional barbed wire is woven into wire, with the development of the economy, the rapid rise of all walks of life, the limitations of the use of traditional barbed wire gradually exposed, such as: aquaculture, to the chicken circle a cage can not be too dense, the wire can not be too thick, woven mesh wire once the mesh over the surface of the net will become soft. We also have the solutions: 1, rolling the straight wire into a wavy shape, but still not enough to feed chickens with mesh can only stretch out the chicken beak can not feed! 2, is electric welding mesh, with the current to the longitude and latitude of the wire spot welding together, mesh do more than most is not restricted.
The corrosion or discoloration of galvanized iron wire in the atmosphere caused by oxygen, moisture and other pollution impurities is called rust or rust. After galvanized iron wire rusting, it will affect the appearance quality, seriously affect the use, and even cause scrap, so galvanized iron wire must be properly kept and pay attention to rust prevention.
Galvanized wire is processed from low carbon steel wire rod, after drawing forming, pickling rust removal, high temperature annealing, cooling and other processes. Galvanized wire is widely used. Electroplating temperature should be controlled at 30 to 50℃. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used.