Hot dip galvanized iron wire using high quality carbon structural steel, after drawing, galvanized iron wire processing. Hot dip galvanized iron wire is widely used in wire mesh, highway guardrail and construction projects. It has the characteristics of thick coating, strong corrosion resistance and strong coating. And according to the special needs of users, according to industry standards to provide various specifications of galvanized wire.
The spring steel wire is made of high carbon and high quality carbon structural steel or carbon tool steel wire rod, and its chemical composition, gas content and non-metallic inclusion must be strictly controlled according to the use of the spring. In order to reduce the appearance of shortcomings and decarbonization layer, the consumption of rod billet to stop surface grinding, if necessary, but also stop peeling.
The life of the “wire”, is actually “low carbon steel wire”, carbon content in less than 0.2%. The surface is usually coated with zinc plating because it is easy to rust. Under atmospheric conditions, the galvanized layer will not rust before most of the fall off, relatively soft. The life of the “steel wire”, is carbon content in about 0.6% of the “carbon steel wire”, or carbon content in about 0.8% of the “high carbon steel wire”, they have enough hardness and elasticity after appropriate heat treatment, high strength. Uses such as winding ordinary spring and so on.
Good galvanized wire, plating thickness of 3- 4 mm, zinc adhesion should be less than 460 grams/m, that is, the average thickness of zinc layer is not less than 65 microns. When the thickness of plated parts is greater than 4 mm, the zinc adhesion should not be less than 610 g/m, that is, the average thickness of zinc layer should not be less than 86 microns. Standard galvanized wire coating must be uniform, galvanized layer basically uniform with copper sulfate solution test etching five times no dew iron. For standard galvanized wire coating adhesion requirements, the zinc layer of plated parts should be firmly combined with the basic metal and have enough adhesion strength, after hammer test does not fall off, not convex.
Due to the influence of production process or other factors, the zinc layer of galvanized wire products will be different to a certain extent, especially ordinary galvanized can not reach the beauty of electric galvanized, ordinary galvanized wire zinc layer is mainly for anticorrosion and corrosion prevention. Large volume galvanized wire products refers to the use of high quality low carbon steel, after drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized, cooling and other processes, some galvanized wire products are made of iron wire galvanized.
Pet cage is generally made of high quality iron wire, low carbon steel wire, stainless steel wire welding, which is characterized by beautiful, lightweight, folding, easy to store. The surface treatment of pet cage is generally: cold galvanized, hot galvanized, spray, dip, chromium plating, nickel plating and other methods.
After the corrosion of impregnated hexagonal wire mesh, the original characteristics will be lost, and the shape, color and mechanical properties will be changed, resulting in equipment damage, pipeline leakage, etc., specifically, it is easy to break and lose the original protection function. Usually, there are three kinds of metal corrosion: physical corrosion, chemical corrosion, electrochemical corrosion, corrosion in addition to the chemical properties and organizational structure of the metal itself, but also related to the surrounding medium, such as wet environment is easier to rust than dry environment, more impurities than impurities less easy corrosion, high temperature conditions than low temperature conditions easy corrosion. After understanding these, we can effectively prevent the corrosion of impregnated six-sided wire mesh, prolong the service life of the product.
That said, it can always deform by pulling hard without changing its integrity, so cold drawing has usually reached a limit, which is not a problem, because without this property it increases hardness, which is the desired effect. Cold wire drawing encountered more rain, when the climate is wet, easy oxidation and rust. Therefore, in the storage process should pay attention to avoid rust.