The galvanized layer forms a special metallurgical structure that can withstand mechanical damage during transportation and use. Selection of low carbon raw materials, through wire drawing, annealing processing, soft and strong tensile resistance. Finished products coated with anti-rust oil, not easy to rust, according to customer requirements into bundles, each bundle of 1-50Kg, can also be made into U-shaped wire, broken wire, internal plastic and external hemp packaging, mainly used for binding silk, construction silk, etc.
There is good toughness and elasticity, simply put, can be easily made into various shapes, and zinc as a coating is silver, very beautiful. Such characteristics make hot dip galvanized wire handicrafts, woven screen and other aspects have also been applied. Hot plating wire selection of high quality low carbon steel rod processing, is the selection of high quality low carbon steel, after drawing molding, pickling rust removal, high temperature annealing, cooling and other processes.
Large coil galvanized wire is made of high quality low carbon steel wire rod processing, is made of high quality low carbon steel, after drawing molding, pickling rust removal, high temperature annealing, hot dip galvanized. Cooling process and other processing. Galvanized wire is divided into hot galvanized wire and cold galvanized wire. Galvanized wire in the process of smelting there are a lot of need to pay more attention to the place, galvanized wire products in the manufacturing process will experience a lot of process, of which the following galvanized wire annealing is a very important step, this step to the nature of galvanized wire has brought a lot of help.
Maintenance is indispensable in the use of galvanized wire. Large coils of galvanized silk should be coated with oil, fiber core immersion oil, oil is required to protect the fiber core is not rotten, not rust, wire moisture fiber, and from the internal lubrication wire rope. Surface coating so that all wire rope strands in the surface, are evenly coated with a layer of rust-proof lubrication grease, which for friction lifting and mineral water large mine rope, to be coated with grinding and water-resistant black oil grease. Coated with red oil with strong film and good rust resistance, it is required to have a thin oil layer, which is easy to keep clean during operation.
Hot dip galvanized wire is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, and the matrix metal forms the infiltration layer, the corrosion resistance is good, the outdoor environment of hot dip galvanized wire can be maintained for decades.
In the atmosphere containing carbon dioxide and hydrogen sulfide and Marine atmosphere is not corrosion resistant, in high temperature and high humidity air and contain organic acid atmosphere is small, galvanized layer is also easy to be corroded. In order to make large rolls of galvanized wire on the surface of the deposited layer to the local, remove the surface film layer, surface inclusions and other defects can be found and treated by conventional techniques. Excess foam is caused by soaps and surfactant saponable fats brought into the tank, and moderate rates of foam formation may be harmless.
After passivation treatment of galvanized layer, a layer of bright old and beautiful color passivation film can be generated, which can significantly improve its protective performance. There are many kinds of galvanized solution, which can be divided into cyanide plating solution and cyanide plating solution. Cyanide galvanizing solution has good dispersion and covering ability, coating crystallization is smooth and fine, simple operation, wide application range, has been used in production for a long time.