Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.
Cold galvanized is in the plating tank through the current unidirectional zinc gradually plated on the metal surface, production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust. Compared with electrogalvanizing, hot galvanizing has lower production cost and less impact on the environment than electroplating.
With a large pickpocket used for steel wire, into the zinc liquid before the surface of the zinc ash stirring; Use a small outlet for galvanized steel wire; Zinc pot steel wire outlet in 30 minutes, with pickpockets back and forth, until the large, floating zinc residue into brown, real zinc ash, zinc ash surface. The extracted zinc ash should be brown yellow real zinc ash, zinc surface, effectively reduce zinc consumption. This is one of the biggest steps to bring zinc consumption down, and it’s a real problem, one that hasn’t been solved for years.
In the process of composite electroplating galvanized wire, the plating solution must be stirred to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. The acid activation solution in the production process can remove the corrosion products and oxide film on the surface of the low carbon steel wire without excessive corrosion on the matrix.
1. Grid structure is simple, beautiful and practical; 2. Easy to transport, installation is not limited by terrain relief; 3. Especially for mountain, slope, multi-curved area adaptability; 4. Medium low price, suitable for large area use. Main market: railway, highway closed net, yard fence, residential guardrail, all kinds of isolation net.
Dip plastic hook net disposal characteristics and downwind, dip plastic is also a common comparison, surface treatment color comparison is single, generally dark green, however, if you want to change into other colors, dip plastic will be more convenient. Because its inner line or inner tube is generally iron line, so, after a period of time, the inner line or inner tube will slowly corrode outward, compared to the outside of the glue fade, hook net will die.
Welding net is made of high quality low carbon steel wire row welding, and then cold plating (electroplating), hot plating, PVC plastic and other surface passivation, plasticizing treatment, smooth surface, uniform mesh, welding spot firm, local machining good performance stability, corrosion resistance, corrosion resistance. Features: stainless steel welding net selection of high quality stainless steel wire row welding, more acid, alkali resistance, welding firm, beautiful, widely used characteristics.
The material of steel structure will affect the organization and thickness of hot dip galvanized film. For example, high tension steel containing silicon, carbon content is high, easy to react with molten zinc quickly, the result of excessive growth of alloying, will cause a grayish black appearance, but does not affect its corrosion resistance. Or heat treated steel, if its tensile strength exceeds 90kg/mm2, after hot dip operation, easy to reduce its strength, etc.
Large roll galvanized wire is the use of low carbon steel wire processing, after drawing forming, pickling rust removal, high temperature annealing, cooling and other processes, in the use of is more widely. The temperature of large roll galvanized wire for electroplating should be controlled at 30 to 50℃. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used.