Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Solid particles or excessive foreign metal impurities in the electroplating solution can cause such problems. Solution: If the coating of large galvanized wire is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.
Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.
Spring steel wire with high carbon quality carbon structural steel or carbon tool steel wire rod production, according to the use of spring strict control of its chemical composition, gas content and non-metallic inclusions. In order to reduce the appearance defect and decarbonization layer, the billet of consumption rod should stop the appearance grinding, and if necessary, stop the peeling.
3. Put zinc block into the plating aid pool regularly, so that the bivalent iron in the plating aid becomes trivalent iron, and it is an important measure to stabilize the PH value in a numerical range. At the same time, it is convenient for the filter to filter out the trivalent iron ions in the plating aid; Ferric ion is controlled between 0.3 and 1.0g/L; When hydrogen is not released in the plating aid, the zinc block is continued. It is an effective measure to reduce zinc slag, improve the fluidity of zinc liquid and reduce the thickness of zinc layer to play the role of plating aid filter.
Large coil galvanized wire in the zinc immersion distance debugging, keep the original speed unchanged, according to t= KD to determine the zinc immersion time (1), where: t is the zinc immersion time is constant, take 4-7D is the diameter of steel wire mm, and then estimate the zinc immersion distance. By adjusting the zinc dip distance, the zinc dip time of steel wire of various specifications can be shortened by 5s on average. In this way, the zinc consumption per ton of steel wire decreases from 61kg to 59.4kg.
There is as far as possible not to show the trace of the application of wire, wire wound flower stems should be wrapped with green or brown tape, in order to cover the trace of the use of wire, in the use of wire modeling can make the drooping flower head raised, and the flower head reinforcement, for herbs and other flower material soft plants, can make the stalk straight. Wire shearing method: if you want to cut the wire, the wire should be straightened and then cut, can not bend the wire, fold and then cut, otherwise, the wire cut is not straight, will bring a small hook, affect the use.
Large hexagonal net called the stone cage net. Stone cage net before delivery, must be folded into a simple surface, packed compression after delivery. Then put it into the right position to open, and then put the appropriate size of the stone into the cage, the lid tight, and then the various stone cage net and adjacent stone cage net tied up.