Hexagonal mesh is made of galvanized iron wire woven by automatic mesh machine, mesh into regular hexagonal shape, mesh standard, beautiful, mesh size can be customized according to customer requirements, usually 27mm,20mm, 13mm, wire diameter from 0.40mm to 1.20mm, to meet the requirements of different customers.
Galvanized wire is processed by low carbon steel wire rod. It is made of low carbon steel, after drawing forming, pickling and rust removal, high temperature annealing, hot dip galvanizing, cooling and other processes. Electrogalvanized iron wire using low carbon steel as raw materials, after drawing, galvanized and other processes completed. It has the characteristics of galvanized layer, strong corrosion resistance, strong galvanized layer, and so on. Galvanized iron wire is widely used in construction, highway walls, Zahua, weaving and other industries.
Hook mesh we usually see everywhere, in fact, hook mesh is a kind of fence, like the highway, stadium fence, road fence, etc., have hook mesh. So what are the effects and advantages of the use of hook net?
Galvanized wire mesh is divided into hot dip galvanized wire mesh and cold galvanized wire mesh. Galvanized steel wire net selects the high quality low carbon steel wire, iron wire factory made by precision of automation machinery welding technology processing, smooth surface, firm structure, integrity is strong, even if the local cutting of galvanized steel wire net, or local also under pressure from loose phenomenon, after molding, wire mesh galvanized corrosion resistance good, has the advantage that the general steel mesh does not have.
Hot dip galvanizing has been used for more than 150 years, and its principle has not changed so far. The steel structure should be fully immersed in zinc at one time to achieve uniform galvanized film structure. If it is too long or too wide to be dipped twice, the zinc layer at the joint will appear rough, too thick and so on. In addition, if the single weight of steel structure is too heavy, it will make its operation difficult if it exceeds the load of galvanizing equipment. Therefore, the communication with the hot dip galvanizing factory in advance.
Large roll galvanized wire is made of low carbon steel wire rod processing, is made of low carbon steel, after drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized. Cooling and other surface treatment process processing. Large roll galvanized wire is divided into hot dip galvanized wire and cold galvanized wire (electric galvanized wire). Although galvanized galvanized wire and silver powder paint spray effect appearance is not much different. But the effect is very different, galvanized wire surface is zinc layer, good adhesion, good corrosion resistance.
The main factors causing metal rust: relative humidity of the atmosphere at the same temperature, the percentage of water vapor content and water vapor saturation content in the atmosphere, known as relative humidity. Under certain relative humidity, the corrosion rate of metal antirust oil is very small, but higher than the relative humidity, the corrosion rate increases suddenly. This relative humidity is called the critical humidity. When the humidity in the atmosphere is higher than the critical humidity, the metal surface will appear water film or water droplets, if the atmosphere contains harmful impurities, dissolved in the water film, water droplets, electrolytes and aggravate corrosion.
Galvanized silk hook mesh is widely used in warehouses, east and west refrigeration, protective reinforcement, park, zoo fence, Marine fishing fence and construction site fence, machinery and equipment protection. There are two kinds of use, that is, slope protection hook net (slope protection net), coal mine hook net (mine hook net, coal mine support net, roadway support net).
Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, Softness is also very uniform, color is also consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding coat hanger, reprocessing industry and so on.
In the process of composite plating, it is necessary to stir the plating solution to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. In the process of production, the acid activation solution can remove the corrosion products and oxide film on the surface of low carbon steel wire without excessive corrosion on the matrix. Galvanized wire can be used zincate galvanized or chloride galvanized and other processes, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire.