Hot – plated wire average performance: reflected in its cross – section, longitudinal uniformity. In the actual process of operation, such as steel wire jitter, the surface scum plating pot and other reasons will cause the surface of galvanized wire galvanized layer accumulation, should strive to solve the problem. In addition to these reasons, we should pay attention to the tooling and process must be stable, and regular testing should be done to ensure the uniformity of the galvanized layer.
The protective duration of the galvanized layer of large roll galvanized wire is closely related to the thickness of the coating. Generally speaking, in relatively dry main gas and indoor use, and in harsh environmental conditions, the thickness of galvanized layer needs to be very high. Therefore, the environmental impact should be considered when choosing the thickness of galvanized layer. After passivation treatment of galvanized layer, a layer of bright old and beautiful color passivation film can be generated, which can significantly improve its protective performance.
This oxide film has greater elasticity and lubricity, does not affect the accuracy of parts. Therefore, the parts of precision instruments and optical instruments, spring steel, thin steel sheet, fine steel wire and so on are commonly bluing treatment. The commonly used galvanizing treatment of large roll galvanized wire is equivalent to forming a protective layer on the surface of the iron wire. The commonly used methods are hot dip galvanizing, hot spray plating, vacuum plating and so on. Different methods have corresponding characteristics.
Spring wire shall have high tensile strength, elastic limit, endurance and fatigue strength, and be resistant to shock and oscillation. The objectives of strength and endurance, especially the prevention of alteration cracks, are key to the consumption of spring steel wires. The inner and outer quality of wire rod directly affect the function of steel wire.
4. When nothing happens, touch the cage in your hand. If your hands are dry, wipe them with an oilcloth and plate them. There are various ways to protect the structure of the cage from damage. The plate cage can improve the surface finish of the cage, and can eliminate the internal stress of part of the bird cage structure, so that the cage structure is gradually stable, reduce the possibility of deformation.
Large roll galvanized wire is divided into hot dip galvanized and cold galvanized two kinds, hot dip galvanized color is dark, consumption of zinc metal, and matrix metal formation of infiltration layer, good corrosion resistance, hot dip galvanized can be maintained for decades in outdoor environment. Cold galvanized production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust.
Hot wire plating adopts zinc-free slag to add hot molten zinc and galvanizing, which avoids the traditional heating process, radiates 1653 hot molten zinc on surface 4102 of zinc liquid surface, and reduces the high temperature oxidation of zinc liquid surface. At the same time, the heating body is in contact with the zinc liquid, and the heat is directly transferred to the zinc liquid. The utilization rate of heat energy can reach more than 90%, and the heat radiation on the zinc liquid surface is reduced.
Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, Softness is also very uniform, color is also consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding coat hanger, reprocessing industry and so on.
Plastic spraying is also we often talk about electrostatic powder spraying, it is the use of electrostatic generator to make plastic powder charged, adsorption on the surface of the iron plate, and then through 180~220 DEG C baking, so that the powder melting adhesion on the metal surface, plastic spraying products are used for indoor use of the box, paint film flat or matte effect. Spray powder mainly acrylic powder, polyester powder, etc.