When galvanized wire is galvanized, it is generally necessary to pay attention to the following problems: the duration of the protective effect of galvanized wire is greatly related to the thickness of the coating. Generally speaking, in the dry main gas and in indoor use, the thickness of galvanized wire galvanized layer only 6-12 μm “, and in harsh environmental conditions, galvanized wire galvanized layer thickness needs 20μm “to B height up to 50μm”. Therefore, the environmental impact should be considered when choosing the thickness of galvanized layer. Galvanized wire in galvanized, pay attention to the above problems, can be well galvanized, to ensure the quality of galvanized wire.
Galvanized wire can be used zincate galvanized or chloride galvanized and other processes, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire. When the galvanized wire out of light plating should be carried out light treatment, the galvanized wire bath to control the temperature. Now the quality level of galvanized wire on the market is not equal, galvanized wire is also called hot dip zinc and hot dip galvanized, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities.
Flexibility because the wire is different from other stainless steel raw materials, it is low density so in the flexibility of the appropriate excellent, it can be described according to people’s fantasy into all kinds of different shapes. Some large enterprises will buy hook flower net products, its reasons are no more than two, one is to prevent people outside the enterprise to walk around at will, the second is to advance the whole image of the enterprise. Therefore, under the premise that the protection requirements are not high, galvanized hook net can play a role in its use, the appearance of flexible hook net is settled to the use of address, from a distance and look at it like a work of art quite appreciate the meaning.
At present, there are two processing methods of blade stabbing rope. One is to make it into a spiral shape, and then make a clip treatment. It is not only our common spiral blade stabbing rope, but also a single spiral blade stabbing rope without clip, but even a single helix can not stretch it to a relatively straight. This is mainly because the blade barbed rope is wrapped and wound at the same time, so it can only be spiral.
Carbon spring steel wire should have high tensile strength, elastic limit, endurance and fatigue strength, and impact and vibration resistance. To ensure the strength and endurance index, especially to avoid changing the occurrence of cracks, is the key to produce spring steel wire. The inner quality and surface quality of the wire rod directly affect the function of the wire.
Cold galvanizing is also called electric galvanizing. It is the use of electrolytic equipment to remove oil, pickling, and then put the pipe into the solution of zinc salt, and connect the anode of the electrolytic equipment, place zinc plate on the opposite side of the pipe, and connect the positive pole of the electrolytic equipment to the power supply. A layer of zinc is deposited on the pipe fitting by directional movement of an electric current from the positive pole to the negative pole. Cold plated pipe fitting is processed before galvanizing.
The production process of large rolls of galvanized wire is a level of drawing, through the mold into a slightly smaller diameter than the original. And so on down to the desired length. One pull is not desirable, must be numbered, from coarse to fine is dependent on metal ductility. If it changes too much it just breaks. After drawing to a certain diameter, galvanized, so that the finished product.
The life of the “wire”, is actually “low carbon steel wire”, carbon content in less than 0.2%. The surface is usually coated with zinc plating because it is easy to rust. Under atmospheric conditions, the galvanized layer will not rust before most of the fall off, relatively soft. The life of the “steel wire”, is carbon content in about 0.6% of the “carbon steel wire”, or carbon content in about 0.8% of the “high carbon steel wire”, they have enough hardness and elasticity after appropriate heat treatment, high strength. Uses such as winding ordinary spring and so on.
There are many categories of large rolls of galvanized wire, and different categories can be applied to different scenarios. The common application of galvanized iron wire is the application of the construction industry. One is the use of binding wire. Whether it is the binding of scaffolding or reinforcement, galvanized iron wire is needed to carry out. There are also 20kg or 50kg bundles of No. 18, No. 16, No. 14, No. 12, No. 10 galvanized coils.