In the process of composite plating, it is necessary to stir the plating solution to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. In the process of production, the acid activation solution can remove the corrosion products and oxide film on the surface of low carbon steel wire without excessive corrosion on the matrix. Galvanized wire can be used zincate galvanized or chloride galvanized and other processes, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire.
Spray powder mainly acrylic powder, polyester powder and so on. Dipping is a kind of plastic coating process, that is, the plastic coating on the matrix, generally metal, such as: daily use of clothes hangers, pliers handles, scissors on the rubber sleeve, various handrails, etc. Plastic immersion is to heat the metal to spray plastic powder evenly on the metal to form a plastic film, or heat immersion liquid into the metal to cool it and then plastic coating on the metal surface.
The difference is that hot dip galvanizing is dipped in zinc solution melted by heating, which has fast production speed and thick but uneven coating. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Cold galvanized is in the plating tank through the current unidirectional zinc gradually plated on the metal surface, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust.
Titanium and titanium alloy with light weight, high strength, corrosion resistance and many other characteristics, titanium and its alloy not only in aviation, aerospace industry has a very important application, and has begun to chemical, petroleum, light industry, power generation, metallurgy and many other civil industrial sectors are widely used. However, titanium and titanium alloy are smaller than steel in terms of hardness and strength. The shortcomings of titanium alloy wire made of titanium alloy in terms of hardness limit its breadth and depth of application.
Hot dip galvanizing is to remove oil from the workpiece, pickling, dipping, drying after dipping into the dissolved zinc solution for a certain time, can be brought out. Hot dip galvanizing is an effective way to prevent corrosion of metal. It is mainly used for metal structure facilities in various industries. It is to immerse the steel parts after rust removal into the melting zinc liquid at about 500℃, so that the surface of the steel members is attached with zinc layer, so as to play the purpose of anti-corrosion. The galvanized layer is more firm.
Corrosion usually metal corrosion has three types: physical, chemical corrosion and electrochemical corrosion, and corrosion depends on the chemistry of the metal itself and the organizational structure, still have relationship with the surrounding medium, such as wet environment than dry environment is easy to rust, more less than the impurities of impurities is easy corrosion, high temperature conditions than under the condition of low temperature corrosion, etc. After knowing these, we can effectively prevent the corrosion of the dip plastic six side wire mesh, prolong the service life of the product.
Plastic spraying is also we often talk about electrostatic powder spraying, it is the use of electrostatic generator to make plastic powder charged, adsorption on the surface of the iron plate, and then through 180~220 DEG C baking, so that the powder melting adhesion on the metal surface, plastic spraying products are used for indoor use of the box, paint film flat or matte effect. Spray powder mainly acrylic powder, polyester powder, etc.
The use of steel mesh saves a lot of on-site binding and construction site, can end civilized construction, advance the quality of steel structure engineering. Because the steel mesh is prefabricated in the factory, there is no need for site reprocessing, and there is no need for steel chips, because the construction cycle is shortened, and the cost of lifting machinery is reduced.
With the development of mining industry, pig iron classification in Our country has been very extensive, to meet the needs of the machinery industry. Generally speaking, iron wire factory produces galvanized iron wire iron can be divided into two categories, is directly from the iron ore through iron tracing exercise out of the metal, the primary components of the ore is iron oxide, silica and other miscellaneous stones. When this ore is specially refined into metal iron, the elements such as carbon, silicon, manganese and so on are mixed in, so that the refined data is called – like general pig iron, also for the initial grade of the material.
Under any application environment, users hope that the welding mesh has better strength, as long as it has improved in strength, it will make better use of the demand, but to make the strength of this product improve, also need to have many conditions, to see what kind of data manufacturers have in production, the strength of the product is the strength of the data, But a manufacturer does not meet the strength requirements in the data, and naturally, it cannot make the strength of the product improve after all, so this is the condition.
Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, The softness is also very uniform, the color is consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding hanger, reprocessing industry, etc.