Because the coating obtained is thicker, hot-dip galvanizing has very good protective function than electric galvanizing, so it is an important maintenance coating for iron and steel parts in strict working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, electric power transportation, shipbuilding and other occupations. In the field of agriculture, such as pesticide irrigation, greenhouse and construction industry such as water and gas transportation, wire casing, scaffolding, Bridges, highway guardrail and other aspects, it has been widely used in these years.
Many people do not know how to choose high quality cut wire, I will give us a detailed introduction. The raw material of cutting wire is divided into: stainless steel cutting wire, copper cutting wire, steel wire cutting wire, copper plated steel wire cutting wire, galvanized steel wire cutting wire, iron wire cutting wire, aluminum wire cutting wire and so on.
During this process, each time the wire is pulled over, the surface hardens due to the high friction temperature. So basically every time you pull it you have to annealing it in the furnace. On the one hand, it is to reduce the surface hardness. On the other hand, during the process of wire pulling, only the surface is deformed, and the center is unchanged. So there’s a lot of stress inside. Therefore, it is necessary to rely on annealing to eliminate the internal stress, so that the wire becomes soft again to eliminate the stress before being drawn again.
Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, Softness is also very uniform, color is also consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding coat hanger, reprocessing industry and so on.
After the optimization of the process, mass production of 0.80mm electro galvanized steel wire electro galvanized zinc layer quality is controlled within 80 ~ 90g/m2, zinc layer quality dispersion is very small; The results show that the average weight of zinc layer is 14.5g/m2, the loss of zinc layer is less than 5%, and the tensile strength of steel wire is 2300 ~ 2500MPa. It not only effectively controls the quality of zinc layer of raw steel wire, but also reduces unnecessary waste and production cost.
The service life of the original galvanized iron welding mesh is very limited. Generally, good iron railings can only be used for about 2 years, and then renovated until the service life, which is not only time-consuming but also has safety risks. After the appearance of zinc-steel railings, the service life has been increased to a great extent in the post-processing. Generally, it can be used for at least 20 years. To improve the service life of zinc steel railings, we first have a brief understanding of the product characteristics of railings. Then from the maintenance aspect, it is necessary to maintain. Maintenance method of electric welding mesh:
Galvanized electric welding mesh refers to the mesh made of zinc alloy material, because of its high strength, high hardness, beautiful appearance, bright color and other advantages, become used in residential communities. Traditional electric welding mesh using iron bars, aluminum alloy materials, need to use welding and other technology, and the texture is soft, easy to rust, single color.