Electro galvanizing shaft wire direct is in the electroplating tank through the current unidirectional zinc gradually plated on the metal surface, production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust. Compared with hot dip galvanizing, electric galvanizing has lower production cost. The difference between cold galvanizing and hot galvanizing: the difference between cold galvanizing and hot galvanizing is that the amount of zinc is different. They can be identified from the color. The color of cold galvanizing is shiny silver white with yellow. Hot dip galvanized shiny hair white.
Hot dip galvanizing is a kind of external treatment technology in the production of fasteners. The common varieties of hot dip galvanizing fasteners are electric galvanizing, powder galvanizing, mechanical galvanizing and hot dip galvanizing. Wire factory according to different requirements of customers for fasteners, different hot-dip galvanized surface treatment. Galvanized layer and steel is a metallurgical connection, become a part of the steel surface, so the durability of the coating is more reliable.
The reason why there are black spots in wire mesh welding is that the action of wire feeding should be timely filled in the melting time, and the development should be appropriate. There is no argon gas, long burning, large current, long distance, blunt tungsten needle and high molten pool temperature are the fundamental reasons for blackening. Continuous burning, is about active welding machine energy selection, machine welding will appear black spots.
To many people, a dog cage looks like a prison, but for dogs who have been raised on cage training, it is their home and shelter. A cage should be a comfortable place. Never put a dog in a cage for no reason. They will see it as punishment. (Why do many dogs fail to adapt to their owners’ commands, because whether the paparazzi can come out or not, it is also seen as a punishment.
In a rainy climate, it is good to find a place with high dry ground. If there is a rain cloth to hide the rain, so much the better. For field operators, please rest assured that the safety and stability of the mesh, especially in the stacking of paper, slight corrosion will not affect the application.
Annealing wire is widely used because it has a good elasticity and flexibility, in the annealing process can be good control of its hardness, it is mainly made of iron wire, more often used in the construction industry binding wire use. In the production of the wire factory, annealing wire will be processed according to the properties of the material, according to the needs of different to change its hardness degree, can make it has more advantages, can reduce the consumption of metal, reduce the cost of production.
No matter how big they are, dogs seem to love touching noses with people and other animals. In fact, nose touching is a form of social interaction for dogs, much like shaking hands and hugging humans. But dogs don’t rub their noses with every person or animal. They choose who to rub their noses with. If they don’t like you or don’t know you at all, they won’t touch your nose. However, adult dogs will touch the nose of almost every puppy. They will not only touch the puppy’s nose, but also smell the puppy.
Large roll galvanized wire is divided into hot dip galvanized and cold galvanized two kinds, hot dip galvanized color is dark, consumption of zinc metal, and matrix metal formation of infiltration layer, good corrosion resistance, hot dip galvanized can be maintained for decades in outdoor environment. Cold galvanized production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust.
There is no adhesion test of powder spraying or fluorocarbon spraying on packaged galvanized wire, but there are two points for reference: first, in sealed or air-free environment, non-metallic volatiles can corrode zinc coating; Second, zinc at higher than 230 degrees (c) will cause the matrix metal brittle. And powder spraying and fluorocarbon spraying are to be baked at a higher temperature and in a sealed environment, causing rapid corrosion of zinc, resulting in loose corrosion film resulting in coating adhesion decline, and even lead to (matrix) steel wire brittle situation may exist.
Some raw materials in the production of unstable processing, the wire itself will exist burr, surface small pits and other local defects. Galvanized steel in galvanized, generally should pay attention to the galvanized layer protection time of galvanized wire, and the thickness of galvanized layer has a great relationship. Generally speaking, when the main gas is relatively dry and used indoors, the galvanized layer thickness of galvanized wires is only 6-12μm, and under relatively harsh conditions, the galvanized layer thickness of galvanized wires needs 20μm, and can be predicted to reach 50μm.
After the corrosion of impregnated hexagonal wire mesh, the original characteristics will be lost, and the shape, color and mechanical properties will be changed, resulting in equipment damage, pipeline leakage, etc., specifically, it is easy to break and lose the original protection function. Usually, there are three kinds of metal corrosion: physical corrosion, chemical corrosion, electrochemical corrosion, corrosion in addition to the chemical properties and organizational structure of the metal itself, but also related to the surrounding medium, such as wet environment is easier to rust than dry environment, more impurities than impurities less easy corrosion, high temperature conditions than low temperature conditions easy corrosion. After understanding these, we can effectively prevent the corrosion of impregnated six-sided wire mesh, prolong the service life of the product.