The production of ROS was studied on white blood cells as a model to screen the effect on eukaryotic cells after being exposed to samples and solar simulated irradiation (according to the level of penetration under the skin). For that purpose, the leukocytes were separated from anticoagulated fresh blood using the Ficoll-Hypaque reactive in a well-known technique [33]. Then, 50 μL of suspensions of P25TiO2NPs (0.2 mg/mL and 0.02 mg/mL), vitaminB2@P25TiO2NPs (0.2 mg/mL and 0.02 mg/mL) and vitamin B2 (0.2 mg/mL and 0.02 mg/mL) were prepared and mixed with 50 μL of white blood cells suspension. A solution of 3% H2O2 was used as positive control and PBS as negative control. Then, the samples were irradiated using the LED panel for 3 and 6 h to simulate the light penetration into the skin. Also, a set of samples was kept in the dark as control. Finally, the ROS were detected through the colorimetric assay employing the nitroblue tetrazolium salt (NBT salt) and the absorbance at 650 nm was measured. The experiment was reproduced twice; the standard deviation was calculated and p-value < 0.05 were considered significant.
Titanium dioxide is an inert earth mineral used as a thickening, opacifying, and sunscreen ingredient in cosmetics. It protects skin from UVA and UVB radiation and is considered non-risky in terms of of skin sensitivity. Because it is gentle, titanium dioxide is a great sunscreen active for sensitive, redness-prone skin. It’s great for use around the eyes, as it is highly unlikely to cause stinging.
Polyvinyl Butyral Resin (PVB) is a solvent Resin synthesized by the acetal reaction of Polyvinyl Alcohol (PVA) and butyraldehyde in contact with coal.
Because Pvb Resin itself contains a lot of hydroxyl groups, it can bridge with some thermosetting resins to improve the properties of chemicals and film hardness.
Because PVB resin has the above excellent characteristics, it is widely used in adhesive safety glass intermediate film of automobile and building, rust cutting primer, baking paint, wood paint, printing ink, adhesive of electronic ceramics and printed circuit board, adhesive between metal and metal, between metal and plastic, modifier of hot-melt adhesive, iron dimension waterproof processing of textile, etc. A variety of new industrial applications are also continuously developed and applied.
The general characteristics of PVB are as follows:
The appearance of polyvinyl butyral (PVB) resin is white spherical porous particles or powder, and its specific gravity is 1:1; However, the filling density is only 0.20 ~ 0.35g/ml.
Thermal properties
The glass transfer temperature (TG) of polyvinyl butyral (PVB) resin ranges from 50 ℃ of low degree of recombination to 90 ℃ of high degree of recombination; The glass transfer temperature can also be adjusted by adding an appropriate amount of Plasticizer to reduce it below 10 ℃.
Mechanical properties
The coating of polyvinyl butyral (PVB) resin has good water resistance, water resistance and oil resistance (it is resistant to aliphatic, mineral, animal and vegetable oils, but not to sesame oil). PVB is widely used in printing inks and coatings because it contains high hydroxyl groups and has good dispersibility to pigments.
In addition, its chemical structure contains both hydrophobic acetal and acetic ACID groups and hydrophilic hydroxyl groups, so PVB has good adhesion to glass, metal, plastic, leather and wood.
Chemical reaction
Any chemical that can react with secondary alcohol will also react with PVB. Therefore, in many applications of PVB, it is often used with thermosetting resin to bridge and harden with the hydroxyl group of PVB, so as to achieve the characteristics of chemical resistance, solvent resistance and water resistance.
Of course, films with different characteristics (such as hardness, toughness, impact resistance, etc.) can be prepared according to different types of thermosetting resin and different mixing ratio with PVB.
Safety properties