With the development of mining industry, the classification of pig iron is already very broad in our country, which can satisfy the demand of mechanical industry. In general, the iron used to produce large rolls of galvanized wire can be divided into two classes. A metal exercised directly from the iron ore through the iron making stroke, the composition of the ore is iron oxide, silica and other miscellaneous stones. When this ore is specially refined into metal iron, carbon, silicon, manganese, and other elements are mixed into it. The material produced in this way is called ordinary pig iron, which is also the material for the first grade.
Remind you to buy galvanized iron wire, should be stored in dry, good ventilation conditions, do not contain corrosive gases, do not mix with the production of organic volatile gas paint, plastic and other substances in a good environment. If conditions, for galvanized parts to increase reliable inner packaging, and put desiccant. If the zinc layer white spots and hair, only mechanical removal, and then normal passivation, or thoroughly washed off the zinc layer after re-plating.
There is no adhesion test of powder spraying or fluorocarbon spraying on packaged galvanized wire, but there are two points for reference: first, in sealed or air-free environment, non-metallic volatiles can corrode zinc coating; Second, zinc at higher than 230 degrees (c) will cause the matrix metal brittle. And powder spraying and fluorocarbon spraying are to be baked at a higher temperature and in a sealed environment, causing rapid corrosion of zinc, resulting in loose corrosion film resulting in coating adhesion decline, and even lead to (matrix) steel wire brittle situation may exist.
1. The surface of the stainless steel pet cage is deposited with dust or alien metal particles containing other metal elements. In the humid air, the condensed water between the attachment and stainless steel will connect the two into a micro cell, which causes the electrochemical reaction and the protective film is destroyed, which is called electrochemical corrosion. To avoid this situation, as long as the stainless steel surface is clean, you can ensure that the stainless steel pet cage does not rust.
Our country industry chooses the low carbon steel with good quality as raw material, and then produces the quality galvanized iron wire by drawing, galvanizing and other processes. Now the production technology of galvanized iron wire products can be divided into hot plating and electroplating two kinds of methods. No matter which one is chosen, it should be carried out in accordance with the corresponding operating specifications, so as to better ensure the production of good products. For key and important parts with tensile strength greater than 1034mpa before plating, the stress should be released at 200±10℃ for more than 1 hour and 140±10℃ before plating.
We must have a certain understanding of the hexagonal network, we are the beautiful shape of the hexagonal network, more than the appearance of the hexagonal network is very beautiful, in fact, the practical value of survival is very high. To introduce the relevant information should be very clearly know the highway guardrail net, hexagonal wire netting in all kinds of fence netting, in the value of the high-speed on the road more MaoJian, it not only be used in all kinds of road, in a sports ball games venue and try our best to take care of landslides, also has reached very matter effectiveness.
Hot dip galvanizing, also known as hot dip galvanizing, is a method of obtaining a metal covering layer by immersing a steel member into a molten zinc solution. With the rapid development of high-voltage power transmission, transportation and communication, the protection requirements for steel parts are becoming higher and higher, and the demand for hot-dip galvanizing is also increasing. Usually the thickness of electrogalvanized layer is 5 ~ 15μm, and the large roll galvanized wire layer is generally more than 35μm, or even up to 200μm. Hot dip galvanized coating ability is good, dense coating, no organic inclusions.
Galvanized wire is processed from low carbon steel wire rod, after drawing forming, pickling rust removal, high temperature annealing, cooling and other processes. Galvanized wire is widely used. Electroplating temperature should be controlled at 30 to 50℃. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used.