The corrosion or discoloration of galvanized iron wire in the atmosphere caused by oxygen, moisture and other pollution impurities is called rust or rust. After galvanized iron wire rusting, it will affect the appearance quality, seriously affect the use, and even cause scrap, so galvanized iron wire must be properly kept and pay attention to rust prevention.
There is as far as possible not to show the trace of the application of wire, wire wound flower stems should be wrapped with green or brown tape, in order to cover the trace of the use of wire, in the use of wire modeling can make the drooping flower head raised, and the flower head reinforcement, for herbs and other flower material soft plants, can make the stalk straight. Wire shearing method: if you want to cut the wire, the wire should be straightened and then cut, can not bend the wire, fold and then cut, otherwise, the wire cut is not straight, will bring a small hook, affect the use.
There are many kinds of galvanized solution, which can be divided into cyanide plating solution and cyanide plating solution. Cyanide galvanizing solution has good dispersion and covering ability, coating crystallization is smooth and fine, simple operation, wide application range, has been used in production for a long time. However, because the plating solution contains highly toxic cyanide, the gas escaping in the plating process is harmful to the health of workers, and the waste water must be treated strictly before discharge.
Good galvanized wire, plating thickness of 3- 4 mm, zinc adhesion should be less than 460 grams/m, that is, the average thickness of zinc layer is not less than 65 microns. When the thickness of plated parts is greater than 4 mm, the zinc adhesion should not be less than 610 g/m, that is, the average thickness of zinc layer should not be less than 86 microns. Standard galvanized wire coating must be uniform, galvanized layer basically uniform with copper sulfate solution test etching five times no dew iron. For standard galvanized wire coating adhesion requirements, the zinc layer of plated parts should be firmly combined with the basic metal and have enough adhesion strength, after hammer test does not fall off, not convex.
Hot dip galvanizing, also known as hot dip galvanizing, is a method of obtaining a metal covering layer by immersing a steel member into a molten zinc solution. With the rapid development of high-voltage power transmission, transportation and communication, the protection requirements for steel parts are becoming higher and higher, and the demand for hot-dip galvanizing is also increasing. Usually the thickness of electrogalvanized layer is 5 ~ 15μm, and the large roll galvanized wire layer is generally more than 35μm, or even up to 200μm. Hot dip galvanized coating ability is good, dense coating, no organic inclusions.
This process has no mold, low processing cost, easy forming, can process a variety of shapes and other characteristics are widely used. But the products of the guardrail are powder impregnated plastic. According to whether it needs heating, it is divided into hot dipping and cold dipping. According to the raw materials of dipping, it can be divided into liquid dipping and powder dipping. Hot-dip galvanizing, as a metal anticorrosion method, is usually to put the steel structure to be derusted into the zinc liquid at about 500℃, so that the zinc layer is attached to the surface of the steel structure.
Cold drawing wire is a metal cold processing, with wire rod as raw material, that is, the mouth of the steel bar. Cold drawing wire is a product produced by a series of processes such as shell stripping, which is a common wire. In the development and production of metal materials, cold drawing wire is a very common material, its performance is good, the range of use is very wide, manufacturers in processing are the use of cold processing to produce.
Annealed wire is a soft iron wire made of low carbon steel cold drawing, heating, constant temperature, heat preservation and other processes. The composition of iron wire varies according to its use. It contains iron, cobalt, nickel, copper, carbon, zinc, and other elements. The hot metal billet rolled into 6.5mm thick steel bar is the wire rod, and then put it into the wire drawing device into a different diameter of the line, and gradually reduce the aperture of the wire tray, cooling, annealing, plating and other processing technology made of various specifications of iron wire.
The strength of the hook mesh should be satisfied: when the vehicle is traveling at 80 kilometers per hour, the hook mesh will not fall into the river when it bumps against the rail at a 15 degree Angle. The shape and color of the hook mesh should be in harmony with the surrounding natural environment. The phenomenon planning of the important Bridges should be done well. When the bridge crosses important traffic lines, such as expressways, urban rail transit, expressways, railway trunk lines, etc., the hook mesh should add the protective mesh on the pavement of the bridge deck.
Hot plating wire can generate thicker coating, and there are both pure zinc layer and iron zinc alloy layer, so the corrosion resistance is better. The production power of hot dip galvanizing is particularly high, and the duration of the parts in the hot dip galvanizing tank usually does not exceed lmin. Compared with galvanizing, hot-dip galvanizing has lower production cost and less environmental impact than galvanizing. To plate, tape, wire, tube and other profiles plating, automation degree is higher.