The tensile strength of cold drawn spring steel wire is slightly higher than that of oil tempered steel wire. The large specification of cold drawn steel wire elastic force is too large, winding the spring is very difficult, so the cold drawn spring steel wire application specification is generally less than 8.0mm, oil quenching tempered steel wire application specification is generally less than 13.0mm. In fact, the diameter of 13.0mm spring is used to light tension spring steel wire, cold drawing wound made into shape and then quenched and tempered. Steel wire with diameter above 15.0mm is mostly made by heating winding process.
For the specification of galvanized wire, the galvanized wire produced by our factory can range from No.8 to No.22, which refers to the BWG standard, that is, from about 4mm to 0.7mm, which can basically cover the type required by the customer. As for the raw material of galvanized wire, normally, we use Q195 mild steel, and some factories will also use SAE1006 or SAE1008. The following is the zinc coating, for galvanized wire, this is very important, the general zinc coating is about 50g/m2 to 80g/m2, some customers need high zinc galvanized wire, zinc coating can reach 200g/m2 to 360g/m2. The tensile strength of galvanized wire is usually 350n/m2 to 800n/m2. Then there is the packaging specification of galvanized wire. The specifications of small rolls of galvanized wire are 50kg/ roll, 100kg/ roll and 200kg/ roll. Of course, there are large rolls of galvanized wire, the weight can reach 300kg/ roll or 800kg/ roll.
Pet cages can be used for indoor and outdoor pet houses. The dog cage is equipped with a fixed food basin and a drinking device, and the rubber pad of the pet cage with a bayonet on the four sides can be assembled. Can be splicing according to the size of the cage, shear, disassembly convenient, easy to clean, can solve the puppy in the ordinary cage pinched foot problem, prevent the puppy in the development of adverse reactions. The bulkhead of the pet cage is breathable and comfortable, which can be used as a heat shield for pets in summer. A puppy with small feet, not a foot, not a pinch.
Any application environment, users want a better the strength of the welded wire mesh, only need to improve its intensity, will make better the habit of using demand, but to be improved in the strength of this product, also need to have the condition of many sided, just need to see factory in produce what kind of material, the strength of the product also is the material strength, But a manufacturer does not meet the strength requirements in the data, after all, there is no way to make the strength of the product progress, so this is the necessary condition.
Wire factory reminds you in the purchase of galvanized wire, should be stored in dry, ventilated conditions, do not contain corrosive gases, do not mix with organic volatile gas produced paint, plastic and other substances in a good environment. If possible, we can add reliable inner packaging for galvanized parts, and put desiccant. If the zinc layer of white spots and long hair, can only be removed by mechanical methods, and then normal passivation, or completely washed off the zinc layer after re-plating.
Generally speaking, in dry main gas and indoor use, the thickness of galvanized coating is only 6-12μm, but under poor environmental conditions, the thickness of galvanized coating is 20μm, can reach 50μm. Therefore, environmental factors should be considered when choosing the thickness of galvanized layer. Galvanized layer after passivation treatment, can naturally form a layer of bright, beautiful color passivation film, can obviously improve its protective function, decorative.
Hot – plated wire average performance: reflected in its cross – section, longitudinal uniformity. In the actual process of operation, such as steel wire jitter, the surface scum plating pot and other reasons will cause the surface of galvanized wire galvanized layer accumulation, should strive to solve the problem. In addition to these reasons, we should pay attention to the tooling and process must be stable, and regular testing should be done to ensure the uniformity of the galvanized layer.