Hot dip galvanizing is then oiled and chromed. The quality of hot-galvanized sheet produced by this method is significantly improved compared with that by wet galvanizing method. It is only valuable for small-scale production. Continuous galvanizing production line includes a series of pretreatment procedures, such as alkali degreasing, hydrochloric acid pickling, water washing, solvent coating, drying, etc., and the original plate needs to be annealed in cover furnace before entering the galvanizing line.
In the process of composite electroplating galvanized wire, the plating solution must be stirred to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. The acid activation solution in the production process can remove the corrosion products and oxide film on the surface of the low carbon steel wire without excessive corrosion on the matrix.
Galvanized wire coating is galvanized, aluminum plated, coated with nylon or plastic, etc. Zinc is divided into thin coating of steel wire after plating and thick coating of galvanized steel wire after drawing. The mechanical properties of thick coating are reduced compared with smooth steel wire rope, which should be used in severe corrosion environment. It is more resistant to corrosion, wear and heat than galvanized wire rope, using the first plating and then drawing method of production. Coated nylon or plastic wire rope is divided into two kinds of coated rope and coated stock after the rope.
Paint on the galvanized layer, the bonding force between each other has a great relationship with the baking temperature of the paint, and alkyd paint is coated after galvanized, and the adhesion is not a problem. After galvanized to do amino paint, paint adhesion is not very good. Do two bottom two surface, adhesion is good, if the two bottom two surface changed to two bottom three surface, that is, more paint, more baked once, again test adhesion is very bad, bad enough to tear the paint from the galvanized layer.
Excellent anticorrosive makes its popularity in the feed, the net surface smooth and tidy, increased the look and feel, can be adornment effect, this characteristic makes it to show in the mining industry, due to high quality with low carbon materials as raw materials, to make it unique general iron mesh screen does not have flexibility, determine its plasticity in use process, Thus can be used in the hardware process of deep processing and manufacturing, complex wall batch swing, underground leakage prevention cracking, light mesh body, so that the cost is much lower than the cost of iron screen, more able to understand its economic and practical.
We basically know that the barbed wire fence generally has two kinds of ring and linear filamentous, the overall protective wire mesh selection of galvanized, stainless steel processing raw materials, long-term use is not easy to rust. Barbed wire fence uses stainless steel barbed wire, plastic coated barbed wire, aluminum coated barbed wire, galvanized barbed wire and other raw materials through special wire drawing into the strand planning, has a strong role in protection and maintenance. Widely used on both sides of the highway, grassland, gardens and other places, because it is a field protection product and therefore updated faster, so how to use the barbed wire fence after abandonment? Here are some of the uses of discarded blades.
Large roll galvanized wire is the use of low carbon steel wire processing, after drawing forming, pickling rust removal, high temperature annealing, cooling and other processes, in the use of is more widely. The temperature of large roll galvanized wire for electroplating should be controlled at 30 to 50℃. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used.
Our country industry chooses the low carbon steel with good quality as raw material, and then produces the quality galvanized iron wire by drawing, galvanizing and other processes. Now the production technology of galvanized iron wire products can be divided into hot plating and electroplating two kinds of methods. No matter which one is chosen, it should be carried out in accordance with the corresponding operating specifications, so as to better ensure the production of good products. For key and important parts with tensile strength greater than 1034mpa before plating, the stress should be released at 200±10℃ for more than 1 hour and 140±10℃ before plating.
The whole welding process of galvanized steel wire mesh does not need special technological methods, good weldability. However, in a few cases, the welding process will present difficulties: the converter steel produced by the old smelting method has high nitrogen content and high impurity content, resulting in high cold brittleness, added aging sensitivity, lower quality of welded joints, and poor weldability.
According to the galvanized iron wire manufacturer, galvanized iron wire is the selection of excellent low carbon steel, through drawing molding, pickling rust removal, high temperature annealing, hot galvanized, cooling and other processes. The following points should be paid attention to in the use of galvanized iron wire:
For the specification of galvanized wire, the galvanized wire produced by our factory can range from No.8 to No.22, which refers to the BWG standard, that is, from about 4mm to 0.7mm, which can basically cover the type required by the customer. As for the raw material of galvanized wire, normally, we use Q195 mild steel, and some factories will also use SAE1006 or SAE1008. The following is the zinc coating, for galvanized wire, this is very important, the general zinc coating is about 50g/m2 to 80g/m2, some customers need high zinc galvanized wire, zinc coating can reach 200g/m2 to 360g/m2. The tensile strength of galvanized wire is usually 350n/m2 to 800n/m2. Then there is the packaging specification of galvanized wire. The specifications of small rolls of galvanized wire are 50kg/ roll, 100kg/ roll and 200kg/ roll. Of course, there are large rolls of galvanized wire, the weight can reach 300kg/ roll or 800kg/ roll.
Paint on the galvanized layer, the binding force between each other and the baking temperature of the paint has a great relationship, after galvanized coating alkyd paint, adhesion is no problem. Galvanized amino paint, paint adhesion is not good. Do two bottom two surface, adhesion is ok, if the two bottom two surface to two bottom three surface, that is, more paint, more baking once, again test adhesion is very poor, poor to the paint from the galvanized layer of pieces torn off.
Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, The softness is also very uniform, the color is consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding hanger, reprocessing industry, etc.