The main difference is carbon content. Iron has a carbon content of 2.11 percent or more, while steel has a carbon content of 2.11 percent or less. Iron-carbon alloys with carbon content of more than 2.11% are cast iron (pig iron), which are basically not malleable and cannot be drawn into wire. Secondly, the content of impurities is different, and the content of harmful impurities such as sulfur and phosphorus in steel is smaller. Wire general color key, wire color light point, white point.
The insulation layer of large rolls of galvanized wire and rigid thermal insulation products can be bound with double strands of galvanized iron wire, and the binding interval shall not exceed 400mm. The pipe or corresponding equipment with nominal diameter equal to or greater than 600mm shall stop reinforcement after binding, and the enclosed galvanized steel wire must be winched. The iron or wood rod should be tightened, but the tightening level should be moderate, not too tight or too loose, and not damage the wire. The consumption of wire and steel wire is generally used in drawing process and galvanized disposal.
Galvanized wire coating has galvanized, aluminum, nylon or plastic coating. Zinc plating is divided into thin coating after steel wire plating and thick coating after steel wire drawing. The mechanical properties of thick coating are lower than that of smooth steel wire rope, and it is suitable for use in serious corrosive environment. Aluminized wire rope it is more resistant to corrosion, wear resistance, heat resistance than galvanized wire rope, using the method of production after the first plating. The wire rope coated with nylon or plastic is divided into two kinds: coated rope and coated rope.
Hook net: hook net also known as diamond net, rhombus net, slope protection net. It is widely used in warehouse, east and west cold storage, protection reinforcement, park, zoo fence, Marine fishing gate and construction site fence, mechanical equipment protection, highway guardrail, sports place purse Seine, road green belt protection net.
Therefore, when zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms diffuse with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with zinc and sinks into the bottom of the hot-dip galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.
As we all know, even if it is the same kind of steel wire, because of the steel making process, wire drawing process and equipment are not the same, so the quality of steel wire production is not the same. Due to the different mechanical properties of steel wire itself, flattening process and equipment, the width and elongation of steel wire in the flattening process have different effects. Therefore, in the selection of wire diameter, the following three factors should be considered:
Galvanized steel pipe is divided into hot dip galvanized and electric galvanized. The layer of hot dip galvanized is thick, the cost of electric galvanized is low, and the surface is not very smooth. Used for steel blowing oxygen pipe, generally with small diameter welded steel pipe, specifications from 3/8-2 inches of eight. Made of 08, 10, 15, 20 or 195-Q235 steel strip, in order to prevent corrosion, some should be aluminized.