And the role of wire mesh in the exterior wall plastering if from an Angle to sail a method of anti-falling, the role of anti-cracking is relatively small, because of the problem of orientation; And about the external insulation system is used in the tile veneer, as for the role should also be anti-drop followed by anti-cracking, so the grid should be selected 10×10×0.6, these are some experience selection, grid conversion from the national provisions of the wire mesh standard, choose the level of steel conversion.
As we all know, iron wire rust is due to contact with water and oxygen chemical reaction, therefore, how to prevent galvanized iron wire rust, first of all, in the storage of galvanized iron wire should choose ventilated dry place, avoid wet or rain leakage, in use, in addition to follow the principle of first in first out, if accidentally caused by the destruction of galvanized layer, should be coated with anti-rust paint treatment, Otherwise, it is easy to lose the protection of galvanized layer and cause galvanized iron wire rust.
Pay attention to safety in line collection and operation, others without the consent of the monitor, Ben have to get on the bus operation. The reels should be placed lightly, stacked firmly and neatly, not more than 5 reels. Direct contact with acid and alkali must be prohibited. When the acid fog exceeds the specified target of the state, measures should be taken to control it in time, otherwise production is not allowed.
Wire factory introduction annealing wire is widely used mainly because it has good elasticity and flexibility, in the process of annealing can be very good control of its soft and hard degree, it is mainly made of iron wire, more often used in the construction industry tied wire use. In the production of annealing wire will be processed according to the performance of the material, according to the demand for different degree of hardness of its soft change, can make it has more advantages, can reduce the consumption of metal, reduce the cost of production.
Large roll galvanized wire is processed by low carbon steel wire rod, through drawing molding, pickling rust removal, high temperature annealing, cooling and other processes. Large roll galvanized wire electroplating temperature should be controlled in 30-50℃. Because of the strong corrosivity of chloride ions in bath, quartz glass heater is generally used. Continuous production does not need heating, but need cooling cooling.
The methods to control the thickness of galvanizing are as follows: you can slow down the lifting speed of the workpiece, control the time of galvanizing as far as possible, add the appropriate amount of thinning alloy, reduce the thickness, and improve the temperature of hot-dip galvanizing. But consider the zinc pot, iron pot should not exceed 480 degrees, ceramic pot can be 530 degrees, which can reduce the time of zinc immersion.
Galvanized wire coating has galvanized, aluminum, nylon or plastic coating. Zinc plating is divided into thin coating after steel wire plating and thick coating after steel wire drawing. The mechanical properties of thick coating are lower than that of smooth steel wire rope, and it is suitable for use in serious corrosive environment. Aluminized wire rope it is more resistant to corrosion, wear resistance, heat resistance than galvanized wire rope, using the method of production after the first plating. The wire rope coated with nylon or plastic is divided into two kinds: coated rope and coated rope.