Cold galvanized, generally speaking, do not need heating, galvanized amount is little, this galvanized parts are easy to fall off in wet environment. Hot dip galvanizing, also known as hot dip galvanizing, is to melt the zinc ingot at high temperature, put some auxiliary materials in, and then dip the metal structural parts into the galvanized groove, so that the metal members are attached to a layer of zinc layer. The advantage of hot dip galvanized is that its anticorrosion ability is strong, the adhesion and hardness of galvanized layer is better.
Large roll galvanized wire is the use of low carbon steel wire processing, after drawing forming, pickling rust removal, high temperature annealing, cooling and other processes, in the use of is more widely. The temperature of large roll galvanized wire for electroplating should be controlled at 30 to 50℃. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used.
When galvanized wire is galvanized, it is generally necessary to pay attention to the following problems: the duration of the protective effect of galvanized wire is greatly related to the thickness of the coating. Generally speaking, in the dry main gas and in indoor use, the thickness of galvanized wire galvanized layer only 6-12 μm “, and in harsh environmental conditions, galvanized wire galvanized layer thickness needs 20μm “to B height up to 50μm”. Therefore, the environmental impact should be considered when choosing the thickness of galvanized layer. Galvanized wire in galvanized, pay attention to the above problems, can be well galvanized, to ensure the quality of galvanized wire.
1. Simple grid structure, beautiful and practical; 2. Easy to transport, installation is not limited by terrain ups and downs; 3. Especially strong adaptability to mountainous, sloping and multi-curved areas; 4. The price is medium and low, suitable for large area. Main market: railway, highway closed network, field fence, district guardrail, all kinds of isolation network.
The main factors causing metal rust: relative humidity of the atmosphere at the same temperature, the percentage of water vapor content and water vapor saturation content in the atmosphere, known as relative humidity. Under certain relative humidity, the corrosion rate of metal antirust oil is very small, but higher than the relative humidity, the corrosion rate increases suddenly. This relative humidity is called the critical humidity. When the humidity in the atmosphere is higher than the critical humidity, the metal surface will appear water film or water droplets, if the atmosphere contains harmful impurities, dissolved in the water film, water droplets, electrolytes and aggravate corrosion.
National standards on the use of wire mesh standards have certain requirements, diameter and mesh size matching use, rather than simply diameter, on the plaster layer to use the mesh should not be greater than 20×20, diameter is not easy to be less than 1mm, just choose diameter is not much meaning, choose 40×40×0.9 and choose 10×10×0.6 wire mesh, Which is better? I’m afraid it’s 10 by 10 by 0.6.
Zinc is a silver-white metal, brittle at room temperature, soluble in acid can also be soluble in alkali, known as amphoteric metal. Pure zinc in dry air is more stable, in humid air or containing carbon dioxide and oxygen water is small, the surface will generate a layer of basic zinc carbonate based thin film layer, it can delay the corrosion rate of zinc layer. The corrosion resistance of zinc coating in aqueous solution of acid, alkali and sodium chloride is stronger.
When large rolls of galvanized wire are used to bind and reinforce the goods, corresponding binding methods should be selected according to the fastening node conditions of the strengthened goods, such as opening binding, opening binding, insertion binding and so on. The insulation layer of semi-hard and soft insulation products shall be based on the diameter of the steel pipe and the size of the equipment. Large rolls of galvanized wire or glue are tied together with a width of 60mm. The binding interval of semi-hard insulating products shall not exceed 300 mm; The larger length of felt and cushion shall not exceed 200mm, and the number of belts shall not be less than 2.
The different spacing of the thorn rope is mainly in order to save costs to consider, because if they are too close, then obviously a little waste of resources, but the installation is too sparse will not work. Usually the bottom spacing is about 10cm, and the top is up to 20cm, this is because the higher the place is more difficult to climb over, usually more than one meter without the help of tools it is difficult for ordinary people to climb over, and the bottom because of the relatively tight can prevent personnel from drilling in the past.