Large hexagonal net called stone cage net, stone cage net before delivery, must be folded into a simple surface, packed compression after delivery. Then put it into the right position to open, and then put the appropriate size of the stone into the cage, the lid tight, and then the various stone cage net and adjacent stone cage net tied up.
Take 20cm galvanized wire for acid fog experiment, check the zinc content of galvanized wire through the balance to see whether it meets the zinc layer standard required by customers, ensure that the metal wire achieves the role of rust and corrosion prevention, and meet the service life required by customers. Galvanized iron wires must be packed in good condition, bound neatly and orderly, and bound inward to prevent scratches during transportation. The inspection standard of galvanized iron wire also includes the tensile test, which is decided according to the material of the galvanized wire order ordered by the customer, and it needs to be tested by comparing the raw material list.
The reason why there are black spots in wire mesh welding is that the action of wire feeding should be timely filled in the melting time, and the development should be appropriate. There is no argon gas, long burning, large current, long distance, blunt tungsten needle and high molten pool temperature are the fundamental reasons for blackening. Continuous burning, is about active welding machine energy selection, machine welding will appear black spots.
Wire mesh first welding after galvanized is through the end of welding and then the company to produce wire mesh wire mesh steel mesh construction mesh, floor heating mesh galvanized or hot dip galvanized. First galvanized after welding is to change wire mesh, after the end of welding can see the solder joint; The two processes are different in price. The cost of plating after welding is low, the appearance is smooth, and the cost of plating after welding is high, and it is not easy to rust.
Pay attention to safety in line collection and operation, others without the consent of the monitor, Ben have to get on the bus operation. The reels should be placed lightly, stacked firmly and neatly, not more than 5 reels. Direct contact with acid and alkali must be prohibited. When the acid fog exceeds the specified target of the state, measures should be taken to control it in time, otherwise production is not allowed.
During this process, each time the wire is pulled over, the surface hardens due to the high friction temperature. So basically every time you pull it you have to annealing it in the furnace. On the one hand, it is to reduce the surface hardness. On the other hand, during the process of wire pulling, only the surface is deformed, and the center is unchanged. So there’s a lot of stress inside. Therefore, it is necessary to rely on annealing to eliminate the internal stress, so that the wire becomes soft again to eliminate the stress before being drawn again.
With a large pickpocket used for steel wire, into the zinc liquid before the surface of the zinc ash stirring; Use a small outlet for galvanized steel wire; Zinc pot steel wire outlet in 30 minutes, with pickpockets back and forth, until the large, floating zinc residue into brown, real zinc ash, zinc ash surface. The extracted zinc ash should be brown yellow real zinc ash, zinc surface, effectively reduce zinc consumption. This is one of the biggest steps to bring zinc consumption down, and it’s a real problem, one that hasn’t been solved for years.
Large roll of galvanized wire alloy elements in iron ore, can make copper through the material thickening degree of strengthening, hardness, impact force, strength resistance, closing rate, elongation, so alloy iron in the exercise of good iron, is an important supplementary element. The difference between galvanized wire and general iron wire is very big, general iron wire is cheap, and because iron is not very stable, easy to rust in wet places, so the stability is not very good, life is not very long.