Greenhouse steel pipe is mainly made of greenhouse composite materials made of pull rod, pressure rod, column, and arch rod to cover the plastic film in a greenhouse. Wire factory introduces its this shape is circular plastic greenhouse, this greenhouse covers a large area, the effect of heat absorption is also very good, convenient to build, the cost of building a is also very low. The raw material source of greenhouse steel pipe is very rich and extensive, and the application effect is good.
In the process of composite electroplating galvanized wire, the plating solution must be stirred to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. The acid activation solution in the production process can remove the corrosion products and oxide film on the surface of the low carbon steel wire without excessive corrosion on the matrix.
The characteristics of these cages are small, light, easy to carry and easy to clean. For small animal cage, the wire diameter of the general iron wire is not very large, the thickness of the plastic is relatively thin, so the use of the time can not be “violence”, otherwise the cage in the “destruction” will occur under the welding or plastic crack.
Hot dip galvanizing is to remove oil from the workpiece, pickling, dipping, drying after dipping into the dissolved zinc solution for a certain time, can be brought out. Hot dip galvanizing is an effective way to prevent corrosion of metal. It is mainly used for metal structure facilities in various industries. It is to immerse the steel parts after rust removal into the melting zinc liquid at about 500℃, so that the surface of the steel members is attached with zinc layer, so as to play the purpose of anti-corrosion. The galvanized layer is more firm.
Hot dip galvanizing, also known as hot dip zinc and hot dip galvanizing, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into the molten zinc liquid at about 500℃, so that the surface of the steel member is attached with zinc layer, so as to play the purpose of anticorrosion.
When the large roll galvanized wire galvanizing process coating foaming, first check the bath temperature. If the bath temperature is not low, then strengthen the plating before removing oil, prevent the matrix metal in acid corrosion. If you pay attention to these problems, the foaming phenomenon still exists, it should pay attention to the amount and quality of additives, then you can stop adding additives, with high current electrolysis for a period of time, in order to reduce the content of additives, observe whether the foaming phenomenon is improved. If there is still no improvement, it is necessary to check whether the storage period of additives is too long, or whether there are too many impurities in the additives.
The guide frame of spray hook net wholesale is composed of guide beam and park core pile, their interval distance is about 3 meters, the spacing of guide beam should be about 1 cm higher than the wall. When installing the guide beam, its position should be far away from the net, and the surround-pile should not be expanded, which will make the surround-pile sink or change its shape.
Heavy hexagonal net, also known as large size hexagonal net, or gabion mesh, made of steel wire by twisting mesh machine. This product is very versatile. Can be used for slope support, foundation pit support, mountain rock surface hanging net shotcrete, slope planting (greening), railway highway isolation barrier, it can also be made of stone cage, stone pad, for rivers, DAMS and seawall anti-erosion protection and reservoirs, river interception with stone cage.
The iron is clean and clean, and then solvent treatment, after drying immersed in zinc liquid, iron and molten zinc reaction to produce an alloyed zinc layer, the process is: degreasing – washing – pickling – assisted plating – drying – hot dip galvanizing – separation – cooling passivation. The thickness of the alloy layer of hot plating wire mainly depends on the chemical composition of the steel silicon content, the size of the steel cross-sectional area, the roughness of the steel surface, the temperature of the zinc pot, the time of dipping zinc, cooling speed, cold rolling deformation, etc.
There is no adhesion test of powder spraying or fluorocarbon spraying on packaged galvanized wire, but there are two points for reference: first, in sealed or air-free environment, non-metallic volatiles can corrode zinc coating; Second, zinc at higher than 230 degrees (c) will cause the matrix metal brittle. And powder spraying and fluorocarbon spraying are to be baked at a higher temperature and in a sealed environment, causing rapid corrosion of zinc, resulting in loose corrosion film resulting in coating adhesion decline, and even lead to (matrix) steel wire brittle situation may exist.