Steel wire after galvanized treatment, the surface will be covered with a layer of zinc metal, to play the role of anti-corrosion, anti-fouling, enhance strength and beauty. The galvanized wire drawing treatment is to process the steel wire by stretching method to obtain a finer, higher strength and smoother surface, and improve its mechanical properties. However, will wire drawing affect the electrical conductivity of galvanized steel wire?
After passivation treatment of galvanized layer, a layer of bright old and beautiful color passivation film can be generated, which can significantly improve its protective performance. There are many kinds of galvanized solution, which can be divided into cyanide plating solution and cyanide plating solution. Cyanide galvanizing solution has good dispersion and covering ability, coating crystallization is smooth and fine, simple operation, wide application range, has been used in production for a long time.
Welding net is widely used in industry, agriculture, breeding, construction, transportation, mining and other aspects. Such as machine shields, animal pens, flower pens, window bars, access fences, poultry cages, egg baskets and home office food baskets, paper baskets and decorative items.
Galvanized steel pipe is divided into hot dip galvanized and electric galvanized. The layer of hot dip galvanized is thick, the cost of electric galvanized is low, and the surface is not very smooth. Used for steel blowing oxygen pipe, generally with small diameter welded steel pipe, specifications from 3/8-2 inches of eight. Made of 08, 10, 15, 20 or 195-Q235 steel strip, in order to prevent corrosion, some should be aluminized.
Thorn rope factory production per ton of product profit is not particularly high so in the sales price to wholesale, many users always think that thorn rope price has a lot of profit space so they are eager to lower the price, some manufacturers in order to sell out on the use of low price promise and then underweight behavior. Often the actual user spends less money with the lack of weight is almost the same, so the unit price is relatively high. Because the quotations of the thorn rope factory are in accordance with the real price, the quality is guaranteed. In this way, the customers will not look for debts after the purchase, and the subsequent purchase work will still find us, so that we can benefit.
The material of the blade can be roughly divided into high quality steel wire, galvanized steel plate, stainless steel plate. The general technology used on the blade: hot dip galvanizing – stamping. The blade has the advantages of corrosion resistance, aging resistance, good weather resistance, easy installation, low price and so on. The use of blade rope: Blade rope has been widely used in military sites, prisons, government, banks, residences, private homes, villas, doors and Windows, roads, railway fences and border lines, etc., to ensure safety. Most prisons basically use razor blades.
When the coating of large galvanized wire is blistered in the process of galvanizing, the bath temperature should be checked first. If the bath temperature is not low, and then strengthen the removal of oil before plating, to prevent the base metal in acid corrosion. If you pay attention to these problems, the bubbling phenomenon still exists, it should pay attention to the dosage and quality of additives, then you can stop adding additives, with high current electrolysis for a period of time, to reduce the content of additives, observe whether the bubbling phenomenon is improved. If there is no improvement, check whether the additive has been stored for too long or whether it contains too many impurities.
Large roll galvanized wire phosphating film is dark gray to black gray, the thickness is generally 5-20μm, has better corrosion resistance in the atmosphere. Membrane is a microporous structure, strong adsorption ability to paint, such as used as paint bottom, corrosion resistance can be further advanced. Metal oxidation treatment: Add steel products to NaOH and NaNO2 mixed solution, heating treatment, the surface can form a layer of thickness of about 0.5-1.5μm blue oxide film, in order to reach the purpose of steel corrosion prevention, this process is called blue treatment, referred to as blue.
Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.
The life of the “wire”, is actually “low carbon steel wire”, carbon content in less than 0.2%. The surface is usually coated with zinc plating because it is easy to rust. Under atmospheric conditions, the galvanized layer will not rust before most of the fall off, relatively soft. The life of the “steel wire”, is carbon content in about 0.6% of the “carbon steel wire”, or carbon content in about 0.8% of the “high carbon steel wire”, they have enough hardness and elasticity after appropriate heat treatment, high strength. Uses such as winding ordinary spring and so on.
When galvanized wire out of the light plating should be carried out light treatment. The bath temperature of galvanized wire should be controlled well. Galvanized wire, also known as hot dip zinc and hot dip galvanized, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into the molten zinc liquid at about 500℃, so that the surface of the steel member is attached with zinc layer, so as to play the purpose of anticorrosion.
Galvanized wire coating is galvanized, aluminum plated, coated with nylon or plastic, etc. Zinc is divided into thin coating of steel wire after plating and thick coating of galvanized steel wire after drawing. The mechanical properties of thick coating are reduced compared with smooth steel wire rope, which should be used in severe corrosion environment. It is more resistant to corrosion, wear and heat than galvanized wire rope, using the first plating and then drawing method of production. Coated nylon or plastic wire rope is divided into two kinds of coated rope and coated stock after the rope.
The height of the shield should not be less than two meters. The length of the shield should be the width of the journey and the extension 10 meters away. The vertical load of the handrail on the bridge is 1.2KM/m, and the horizontal external load is 2.5KM/m, both of which should be calculated separately. Galvanized hook mesh is attributed to a hook mesh, it is the selection of galvanized wire, hot dip galvanized wire as raw materials, woven through the hook mesh crimping truncated.