The formation process of hot dip galvanized layer is between the iron matrix and the outside of the pure zinc layer, the formation of iron-zinc alloy process, the workpiece surface in hot dip plating when the formation of iron-zinc alloy layer, so that the iron and pure zinc layer is well combined. The process of large roll galvanized wire can be simply described as: when the iron workpiece is immersed in the molten zinc liquid, the first zinc and α-iron (body-centered) solid melt is formed on the interface. This is a crystal formed by the matrix metal iron dissolved with zinc atoms in the solid state. The two metal atoms are fused with each other, and the attraction between the atoms is relatively small.
Hot dip galvanized iron wire using high quality carbon structural steel, after drawing, galvanized iron wire processing. Hot dip galvanized iron wire is widely used in wire mesh, highway guardrail and construction projects. It has the characteristics of thick coating, strong corrosion resistance and strong coating. And according to the special needs of users, according to industry standards to provide various specifications of galvanized wire.
The formation process of hot dip galvanized layer is between the iron matrix and the outside of the pure zinc layer, the formation of iron-zinc alloy process, the workpiece surface in hot dip plating when the formation of iron-zinc alloy layer, so that the iron and pure zinc layer is well combined. The process of large roll galvanized wire can be simply described as: when the iron workpiece is immersed in the molten zinc liquid, the first zinc and α-iron (body-centered) solid melt is formed on the interface. This is a crystal formed by the matrix metal iron dissolved with zinc atoms in the solid state. The two metal atoms are fused with each other, and the attraction between the atoms is relatively small.
Hot plating wire mixed rare earth and aluminum elements, make zinc liquid fluidity, more uniform coating, but also reduce zinc consumption. Hot-dip galvanized wire has better protective properties than cold galvanized wire, which makes it widely used in chemical experiment equipment. Hot plated wire coating is thick, so that it has good corrosion resistance, can be in the outdoor sun and rain and other harsh environment can be maintained for decades, so hot galvanized wire is widely used in construction, traffic guardrail and other outdoor facilities.
For the wide use of screen, the state has regulations. You also specify the diameter size, mesh size, or usage method. For plastering nets, the mesh should be less than 20 and the diameter should be greater than 1 mm. Not only are specifications specified, but safety is preferred if wire mesh is used in exterior plastering nets. If you fall, the consequences are unimaginable. Therefore, the application of norms should be combined with reality.
Generally, due to wet weather and more precipitation, oxidation and rust of binding iron wire NetEase occurs, so we should better store and use galvanized iron wire to avoid rust as far as possible. About the barbed wire, the surface of the barbed wire attached a layer of galvanized layer, the galvanized layer if too thick will not meet the SGS environmental standards. But if it is too thin, it is easy to oxidize with water molecules and rust.